Workpiece cutting method and semiconductor chip

ABSTRACT

An object cutting method includes a first step of preparing an object including a single crystal material substrate and a functional device layer provided on a first main surface side, a second step of irradiating the object with laser light to form at least one row of modified regions in the substrate and to form a fracture in the object so as to extend between the at least one row of modified regions and a second main surface of the object, and a third step of performing dry etching on the object from the second main surface side to form a groove opening to the second main surface, in the object. In the third step, the at least one row of modified regions is removed to form an uneven region which has an uneven shape and in which single crystal silicon is exposed, in an inner surface of the groove.

TECHNICAL FIELD

The present disclosure relates to an object cutting method and a semiconductor chip.

BACKGROUND ART

An object cutting method of cutting an object to be processed into a plurality of semiconductor chips along each of a plurality of lines to cut in a manner that at least one row of modified regions is formed in the object along each of the plurality of lines to cut, by irradiating the object with laser light, and then an extension film stuck to the object is extended is known (for example, see Patent Literature 1).

CITATION LIST Patent Literature

Patent Literature 1: Japanese Patent No. 4781661

SUMMARY OF INVENTION Technical Problem

In the object cutting method as described above, the object is cut into the plurality of semiconductor chips in a manner that extension film is extended, and thus fractures extended from the modified region are caused to reach both main surfaces of the object, in some cases. However, a portion of the object, which is not cut into the plurality of semiconductor chips, may remain.

An object of the present disclosure is to provide an object cutting method and a semiconductor chip in which it is possible to reliably cut an object to be processed into a plurality of semiconductor chips.

Solution to Problem

According to an aspect of the present disclosure, an object cutting method includes a first step of preparing an object to be processed including a single crystal silicon substrate and a functional device layer provided on a first main surface side, a second step of, after the first step, irradiating the object with laser light to form at least one row of modified regions in the single crystal silicon substrate along each of a plurality of lines to cut and to form a fracture in the object so as to extend between the at least one row of modified regions and a second main surface of the object along each of the plurality of lines to cut, and a third step of, after the second step, performing dry etching on the object from the second main surface side to form a groove opening to the second main surface, in the object along each of the plurality of lines to cut. In the third step, the dry etching is performed from the second main surface side such that the at least one row of modified regions is removed to form an uneven region which has an uneven shape corresponding to the removed modified region and in which single crystal silicon is exposed, in an inner surface of the groove.

In the object cutting method, the dry etching is performed from the second main surface side, on the object in which the fracture is formed to extend between the at least one row of modified regions and the second main surface of the object. Thus, the dry etching selectively progresses from the second main surface side along the fracture, and the groove in which an opening is narrow in width and deep is formed along each of the plurality of lines to cut. Thus, it is possible to reliably cut the object into a plurality of semiconductor chips along each of the lines to cut, by extending an extension film stuck to the second main surface side to which the groove opens, for example. In addition, since the uneven region in which single crystal silicon is exposed is formed by removing the at least one row of modified regions, it is possible to suppress a decrease of strength in the vicinity of the uneven region.

In the object cutting method in the aspect of the present disclosure, in the second step, the at least one row of modified regions may be formed along each of the plurality of lines to cut by forming a plurality of rows of modified regions arranged in a thickness direction of the object, and the fracture may be formed to extend between modified regions adjacent to each other among the plurality of rows of modified regions. In the third step, the dry etching may be performed from the second main surface side such that the modified region on the second main surface side among the plurality of rows of modified regions is removed to form the uneven region which has the uneven shape corresponding to the removed modified region, in the inner surface of the groove. According to this configuration, it is possible to cause the dry etching to selectively progress deeper.

In the object cutting method in the aspect of the present disclosure, in the second step, the at least one row of modified regions may be formed along each of the plurality of lines to cut by forming a plurality of modified spots arranged along each of the plurality of lines to cut, and the fracture may be formed to extend between modified spots adjacent to each other among the plurality of modified spots. According to this configuration, it is possible to cause the dry etching to selectively progress with higher efficiency.

The object cutting method in the aspect of the present disclosure may further include a fourth step of, after the third step, cutting the object into the plurality of semiconductor chips along each of the plurality of lines to cut by sticking an extension film to the second main surface side and extending the extension film. According to this configuration, it is possible to reliably cut the object into the plurality of semiconductor chips along each of the lines to cut. Further, since the plurality of semiconductor chips is spaced from each other on the extension film, it is possible to easily pick the semiconductor chips up.

According to another aspect of the present disclosure, an object cutting method includes a first step of preparing an object to be processed including a single crystal material substrate and a functional device layer provided on a first main surface side, a second step of, after the first step, irradiating the object with laser light to form at least one row of modified regions in the single crystal material substrate along each of a plurality of lines to cut and to form a fracture in the object so as to extend between the at least one row of modified regions and a second main surface of the object along each of the plurality of lines to cut, and a third step of, after the second step, performing dry etching on the object from the second main surface side to form a groove opening to the second main surface, in the object along each of the plurality of lines to cut. In the third step, the dry etching is performed from the second main surface side such that the at least one row of modified regions is removed to form an uneven region which has an uneven shape corresponding to the removed modified region and in which a single crystal material is exposed, in an inner surface of the groove.

In the object cutting method, the dry etching is performed from the second main surface side, on the object in which the fracture is formed to extend between the at least one row of modified regions and the second main surface of the object. Thus, the dry etching selectively progresses from the second main surface side along the fracture, and the groove in which an opening is narrow in width and deep is formed along each of the plurality of lines to cut. Thus, it is possible to reliably cut the object into a plurality of semiconductor chips along each of the lines to cut, by extending an extension film stuck to the second main surface side to which the groove opens, for example. In addition, since the uneven region in which the single crystal material is exposed is formed by removing the at least one row of modified regions, it is possible to suppress a decrease of strength in the vicinity of the uneven region.

In the object cutting method in the aspect of the present disclosure, in the second step, the at least one row of modified regions may be formed along each of the plurality of lines to cut by forming a plurality of rows of modified regions arranged in a thickness direction of the object, and the fracture may be formed to extend between modified regions adjacent to each other among the plurality of rows of modified regions. In the third step, the dry etching may be performed from the second main surface side such that the modified region on the second main surface side among the plurality of rows of modified regions is removed to form the uneven region which has the uneven shape corresponding to the removed modified region, in the inner surface of the groove. According to this configuration, it is possible to cause the dry etching to selectively progress deeper.

In the object cutting method in the aspect of the present disclosure, in the second step, the at least one row of modified regions may be formed along each of the plurality of lines to cut by forming a plurality of modified spots arranged along each of the plurality of lines to cut, and the fracture may be formed to extend between modified spots adjacent to each other among the plurality of modified spots. According to this configuration, it is possible to cause the dry etching to selectively progress with higher efficiency.

The object cutting method in the aspect of the present disclosure may further include a fourth step of, after the third step, cutting the object into the plurality of semiconductor chips along each of the plurality of lines to cut by sticking an extension film to the second main surface side and extending the extension film. According to this configuration, it is possible to reliably cut the object into the plurality of semiconductor chips along each of the lines to cut. Further, since the plurality of semiconductor chips is spaced from each other on the extension film, it is possible to easily pick the semiconductor chips up.

According to still another aspect of the present disclosure, a semiconductor chip includes a single crystal silicon substrate, and a functional device layer provided on a first surface side of the single crystal silicon substrate. A portion of the single crystal silicon substrate on at least second surface side has a shape which becomes thinner as becoming farther from the first surface. An uneven region which has an uneven shape and in which single crystal silicon is exposed is formed in a band shape on a side surface of the portion.

In the semiconductor chip, it is possible to cause the uneven region to function as a gettering region of capturing impurities. Since single crystal silicon is exposed in the uneven region, it is possible to suppress the decrease of strength in the vicinity of the uneven region.

Advantageous Effects of Invention

According to the present disclosure, it is possible to provide an object cutting method and a semiconductor chip in which it is possible to reliably cut an object to be processed into a plurality of semiconductor chips.

BRIEF DESCRIPTION OF DRAWINGS

FIG. 1 is a schematic structural diagram of a laser processing apparatus used for forming a modified region.

FIG. 2 is a plan view of an object to be processed as a target for forming the modified region.

FIG. 3 is a sectional view of the object taken along the line of FIG. 2.

FIG. 4 is a plan view of the object after laser processing.

FIG. 5 is a sectional view of the object taken along the line V-V of FIG. 4.

FIG. 6 is a sectional view of the object taken along the line VI-VI of FIG. 4.

FIG. 7 is a sectional view illustrating an experimental result on an object cutting method.

FIG. 8 is a sectional view illustrating an experimental result on the object cutting method.

FIG. 9 is a sectional view illustrating an experimental result on the object cutting method.

FIG. 10 is a sectional view illustrating an experimental result on the object cutting method.

FIG. 11 is a diagram illustrating an experimental result on the object cutting method.

FIG. 12 is a diagram illustrating an experimental result on the object cutting method.

FIG. 13 is a diagram illustrating an experimental result on the object cutting method.

FIG. 14 is a diagram illustrating an experimental result on the object cutting method.

FIG. 15 is a diagram illustrating an experimental result on the object cutting method.

FIG. 16 is a diagram illustrating an experimental result on the object cutting method.

FIG. 17 is a diagram illustrating an experimental result on the object cutting method.

FIG. 18 is a diagram illustrating an experimental result on the object cutting method.

FIG. 19 is a diagram illustrating an experimental result on the object cutting method.

FIG. 20 is a diagram illustrating an experimental result on the object cutting method.

FIG. 21 is a perspective view of the object illustrating an experimental result on the object cutting method.

FIG. 22 is a sectional view illustrating an object cutting method according to a first embodiment.

FIG. 23 is a sectional view illustrating the object cutting method according to the first embodiment.

FIG. 24 is a sectional view illustrating the object cutting method according to the first embodiment.

FIG. 25 is a sectional view illustrating the object cutting method according to the first embodiment.

FIG. 26 is a perspective view of a semiconductor chip illustrating the object cutting method according to the first embodiment.

FIG. 27 is a diagram illustrating the object cutting method according to the first embodiment.

FIG. 28 is a sectional view illustrating the object cutting method according to the first embodiment.

FIG. 29 is a sectional view illustrating the object cutting method according to the first embodiment.

FIG. 30 is a sectional view illustrating the object cutting method according to the first embodiment.

FIG. 31 is a sectional view illustrating the object cutting method according to the first embodiment.

FIG. 32 is a perspective view of the semiconductor chip illustrating the object cutting method according to the first embodiment.

FIG. 33 is a sectional view illustrating the object cutting method according to the first embodiment.

FIG. 34 is a sectional view illustrating the object cutting method according to the first embodiment.

FIG. 35 is a sectional view illustrating the object cutting method according to the first embodiment.

FIG. 36 is a sectional view illustrating the object cutting method according to the first embodiment.

FIG. 37 is a sectional view illustrating the object cutting method according to the first embodiment.

FIG. 38 is a sectional view illustrating the object cutting method according to the first embodiment.

FIG. 39 is a sectional view illustrating an object cutting method according to a second embodiment.

FIG. 40 is a sectional view illustrating the object cutting method according to the second embodiment.

FIG. 41 is a sectional view illustrating the object cutting method according to the second embodiment.

FIG. 42 is a sectional view illustrating the object cutting method according to the second embodiment.

FIG. 43 is a sectional view illustrating an object cutting method according to a third embodiment.

FIG. 44 is a sectional view illustrating the object cutting method according to the third embodiment.

FIG. 45 is a sectional view illustrating the object cutting method according to the third embodiment.

FIG. 46 is a sectional view illustrating the object cutting method according to the third embodiment.

FIG. 47 is a sectional view illustrating the object cutting method according to the third embodiment.

FIG. 48 is a sectional view illustrating the object cutting method according to the third embodiment.

FIG. 49 is a sectional view illustrating the object cutting method according to the third embodiment.

FIG. 50 is a sectional view illustrating the object cutting method according to the third embodiment.

FIG. 51 is a sectional view illustrating the object cutting method according to the third embodiment.

FIG. 52 is a sectional view illustrating an object cutting method according to a fourth embodiment.

FIG. 53 is a sectional view illustrating the object cutting method according to the fourth embodiment.

FIG. 54 is a sectional view illustrating the object cutting method according to the fourth embodiment.

FIG. 55 is a sectional view illustrating the object cutting method according to the fourth embodiment.

DESCRIPTION OF EMBODIMENTS

Hereinafter, embodiments of the present disclosure will be explained in detail with reference to drawings. In the drawings, the same or equivalent parts will be denoted by the same reference signs, without redundant description.

In an object cutting method according to an embodiment, laser light is converged at an object to be processed to form a modified region within the object along a line to cut. Therefore, forming of the modified region will be explained at first with reference to FIGS. 1 to 6.

As illustrated in FIG. 1, a laser processing apparatus 100 includes a laser light source 101 that causes laser light L to oscillate in a pulsating manner and is a laser light emission unit, a dichroic mirror 103 disposed to change a direction of the optical axis (optical path) of the laser light L by 90°, and a converging lens 105 configured to converge the laser light L. The laser processing apparatus 100 further includes a support table 107 for supporting an object to be processed 1 irradiated with the laser light L converged by the converging lens 105, a stage 111 for moving the support table 107, a laser light source controller 102 for controlling regulating the laser light source 101 in order to adjust the output (pulse energy, light intensity), the pulse width, the pulse waveform, and the like of the laser light L, and a stage controller 115 for regulating the movement of the stage 111.

In the laser processing apparatus 100, the laser light L emitted from the laser light source 101 changes the direction of its optical axis by 90° with the dichroic mirror 103 and then is converged by the converging lens 105 into the object 1 mounted on the support table 107. At the same time, the stage 111 is shifted, so that the object 1 moves relative to the laser light L along a line 5 to cut. This forms a modified region in the object 1 along the line 5 to cut. While the stage 111 is shifted here for relatively moving the laser light L, the converging lens 105 may be shifted instead or together therewith.

Employed as the object 1 is a planar member (for example, a substrate or a wafer), examples of which include semiconductor substrates formed of semiconductor materials and piezoelectric substrates formed of piezoelectric materials. As illustrated in FIG. 2, in the object 1, the line 5 to cut is set for cutting the object 1. The line 5 to cut is a virtual line extending straight. When forming a modified region within the object 1, the laser light L is relatively moved along the line 5 to cut (that is, in the direction of arrow A in FIG. 2) while locating a converging point (converging position) P within the object 1 as illustrated in FIG. 3. This forms a modified region 7 in the object 1 along the line 5 to cut as illustrated in FIG. 4, FIG. 5 and FIG. 6, and the modified region 7 formed along the line 5 to cut acts as a cutting start region 8.

The converging point P is a position at which the laser light L is converged. The line 5 to cut may be curved instead of being straight, a three-dimensional one combining them, or one specified by coordinates. The line 5 to cut may be one actually drawn on a front surface 3 of the object 1 without being restricted to the virtual line. The modified region 7 may be formed either continuously or intermittently. The modified region 7 may be formed either in rows or dots and may be formed at least in the object 1. There are cases where fractures are formed from the modified region 7 acting as a start point, and the fractures and modified region 7 may be exposed at outer surfaces (front surface 3, rear surface, and outer peripheral surface) of the object 1. The laser light entrance surface for forming the modified region 7 is not limited to the front surface 3 of the object 1 but may be the rear surface of the object 1.

In a case where the modified region 7 is formed in the object 1, the laser light L is transmitted through the object 1 and absorbed, in particular, in the vicinity of the converging point P in the object 1. Thus, the modified region 7 is formed in the object 1 (that is, internal absorption laser processing). In this case, the front surface 3 of the object 1 hardly absorbs the laser light L, and thus does not melt. In a case where the modified region 7 is formed on the front surface 3 or the rear surface of the object 1, the laser light L is absorbed, in particular, in the vicinity of the converging point P on the front surface 3 or the rear surface. Thus, the front surface 3 or the rear surface is melted and removed, and a removed portion such as a hole or a groove is formed (surface absorption laser processing).

The modified region 7 refers to a region having physical characteristics such as density, a refractive index, and mechanical strength, which have attained states different from those of their surroundings. Examples of the modified region 7 include molten processed regions (meaning at least one of regions resolidified after having been once molten, those in the molten state, and those in the process of resolidifying from the molten state), crack regions, dielectric breakdown regions, refractive index changed regions, and their mixed regions. Other examples of the modified region 7 include areas where the density of the modified region 7 has changed from that of an unmodified region and areas formed with a lattice defect in a material of the object 1. In a case where the material of the object 1 is single crystal silicon, the modified region 7 also refers to a high dislocation density region.

The molten processed regions, refractive index changed regions, areas where the modified region 7 has a density different from that of the unmodified region, and areas formed with a lattice defect may further incorporate a fracture (cut or microcrack) therein or at an interface between the modified region 7 and the unmodified region. The incorporated fracture may be formed over the whole surface of the modified region 7 or in only some or a plurality of parts thereof. The object 1 includes a substrate made of a crystal material having a crystal structure. For example, the object 1 includes a substrate made of at least any of gallium nitride (GaN), silicon (Si), silicon carbide (SiC), LiTaO₃, and sapphire (Al₂O₃). In other words, the object 1 includes a gallium nitride substrate, a silicon substrate, a SiC substrate, a LiTaO₃ substrate, or a sapphire substrate, for example. The crystal material may be either anisotropic crystal or isotropic crystal. The object 1 may include a substrate made of an amorphous material having an amorphous structure (non-crystalline structure) or may include, for example, a glass substrate.

In the embodiment, the modified region 7 can be formed by forming a plurality of modified spots (processing scars) along the line 5 to cut. In this case, the modified region 7 is formed by integrating the plurality of modified spots. The modified spot is a modified portion formed by a shot of one pulse of pulsed laser light (that is, one pulse of laser irradiation: laser shot). Examples of the modified spots include crack spots, molten processed spots, refractive index changed spots, and those in which at least one of them is mixed. As for the modified spots, their size and lengths of fractures occurring therefrom can be controlled as necessary in view of the required cutting accuracy, the demanded flatness of cut surfaces, the thickness, kind, and crystal orientation of the object 1, and the like. In the embodiment, the modified spots can be formed along the line 5 to cut, for the modified region 7.

[Experimental Result on Object Cutting Method]

Firstly, an example of an object cutting method will be explained with reference to FIGS. 7 to 10. Constituents illustrated in FIGS. 7 to 10 are schematic, and an aspect ratio and the like of each constituent are different from those of the practical one.

As illustrated in FIG. 7(a), an object to be processed 1 including a single crystal silicon substrate 11 and a functional device layer 12 provided on a first main surface 1 a side is prepared, and a protective film 21 is stuck to the first main surface 1 a of the object 1. The functional device layer 12 includes a plurality of functional devices 12 a (light receiving device such as a photodiode, a light emitting device such as a laser diode, or a circuit device formed as a circuit, and the like) arranged along the first main surface 1 a in a matrix, for example. A second main surface 1 b of the object 1 (main surface on an opposite side of the first main surface 1 a) is a surface of the single crystal silicon substrate 11 on an opposite side of the functional device layer 12.

As illustrated in FIG. 7(b), if the object 1 is irradiated with laser light L by using the second main surface 1 b as a laser light entrance surface, a plurality of rows of modified regions 7 is formed in the single crystal silicon substrate 11 along each of a plurality of lines 5 to cut, and a fracture 31 is formed in the object 1 along each of the plurality of lines 5 to cut. The plurality of lines 5 to cut is set in, for example, a grid so as to pass between the functional device 12 a adjacent to each other in a case of being viewed from a thickness direction of the object 1. A plurality of rows of modified regions 7 formed along each of the plurality of lines 5 to cut is arranged in the thickness direction of the object 1. The fracture 31 extends at least between one row of modified regions 7 on the second main surface 1 b side and the second main surface 1 b.

If, as illustrated in FIG. 8(a), dry etching is performed on the object 1 from the second main surface 1 b side, a groove 32 is formed in the object 1 along each of the plurality of lines 5 to cut, as illustrated in FIG. 8(b). The groove 32 is, for example, a V groove (groove having a V-shaped section) opening to the second main surface 1 b. Dry etching selectively progresses from the second main surface 1 b side along the fracture 31 (that is, along each of the plurality of lines 5 to cut), and thereby the groove 32 is formed. Then, an uneven region 9 is formed on the inner surface of the groove 32 in a manner that one row of modified region 7 on the second main surface 1 b side is removed by dry etching. The uneven region 9 has an uneven shape corresponding to the one row of modified regions 7 on the second main surface 1 b side. Details thereof will be described later.

Performing dry etching on the object 1 from the second main surface 1 b side has the meaning that dry etching is performed on the single crystal silicon substrate 11 in a state where the first main surface 1 a is covered with the protective film and the like, and the second main surface 1 b (or etching protection layer (described later) 23 in which a gas passage region is formed along each of the plurality of lines 5 to cut) is exposed to an etching gas. In particular, in a case of performing reactive ion etching (plasma etching), performing dry etching means irradiation of the second main surface 1 b (or etching protection layer (described later) 23 in which a gas passage region is formed along each of the plurality of lines 5 to cut) with reactive species in plasma.

Then, as illustrated in FIG. 9(a), an extension film 22 is stuck to the second main surface 1 b of the object 1. As illustrated in FIG. 9(b), the protective film 21 is removed from the first main surface 1 a of the object 1. As illustrated in FIG. 10(a), if the extension film 22 is extended, the object 1 is cut into a plurality of semiconductor chips 15 along each of the plurality of lines 5 to cut. Then, as illustrated in FIG. 10(b), the semiconductor chips 15 are picked up.

Next, an experimental result in a case of performing dry etching after the modified region is formed as in the above-described example of the object cutting method will be explained.

In a first experiment (see FIGS. 11 and 12), a plurality of lines to cut was set in stripes on a single crystal silicon substrate having a thickness of 400 μm, at an interval of 2 mm. Then, a plurality of rows of modified regions arranged in a thickness direction of the single crystal silicon substrate was formed in the single crystal silicon substrate along each of the plurality of lines to cut. (a) in FIG. 11 is a section picture (accurately, picture of a cut surface when the single crystal silicon substrate is cut before reactive ion etching described later is performed) of the single crystal silicon substrate after the modified region is formed. (b) in FIG. 11 is a plan picture of the single crystal silicon substrate after the modified region is formed. Hereinafter, the thickness direction of the single crystal silicon substrate is simply referred to as “the thickness direction”, and one surface (in (a) in FIG. 11, upper surface of the single crystal silicon substrate) in a case where dry etching is performed on the single crystal silicon substrate from the one surface side is simply referred to as “one surface”.

In FIG. 11, “standard processing, surface: HC” means a state where one row of modified regions on one surface side is separated from the one surface, and a fracture reaches the one surface from the one row of modified regions, in a case where laser light is converged by natural spherical aberration (aberration which occurs naturally at a converging position in accordance with Snell's law or the like due to converging of the laser light on the object), and a state where fractures respectively extending from the modified region in the thickness direction are connected to each other. “Tact-up processing, surface: HC” means a state where one row of modified regions on one surface side is separated from the one surface, and a fracture reaches the one surface from the one row of modified regions, in a case where laser light is converged such that the length of a converging point in an optical axis direction becomes shorter than natural spherical aberration by aberration correction, and a state where fractures respectively extending from the modified region in the thickness direction are connected to each other at black streak portions viewed in (a) in FIG. 11.

“VL pattern processing surface: HC” means a state where one row of modified regions on one surface side is separated from the one surface, and a fracture reaches the one surface from the one row of modified regions, in a case where laser light is converged such that the length of the converging point in the optical axis direction becomes longer than natural spherical aberration by imparting aberration. “VL pattern processing surface: ST” means a state where one row of modified regions on one surface side is separated from the one surface, and a fracture does not reach the one surface from the one row of modified regions, in a case where laser light is converged such that the length of the converging point in the optical axis direction becomes longer than natural spherical aberration by imparting aberration. “VL pattern processing surface: ablation” means a state where one row of modified regions on one surface side is exposed to the one surface in a case where laser light is converged such that the length of the converging point in the optical axis direction becomes longer than natural spherical aberration by imparting aberration.

After the modified regions were formed as described above, reactive ion etching with CF₄ (carbon tetrafluoride) was performed on the one surface of the single crystal silicon substrate for 60 minutes. FIG. 12 illustrates results thereof. (a) in FIG. 12 is a plan picture of the single crystal silicon substrate after reactive ion etching is performed. (b) in FIG. 12 is a section picture (picture of a cut surface perpendicular to the line to cut) of the single crystal silicon substrate after reactive ion etching is performed.

Here, definitions of terms illustrated in FIG. 12 will be explained with reference to FIG. 13. “Groove width” indicates a width W of an opening of a groove formed by dry etching. “Groove depth” indicates a depth D of the groove formed by dry etching. “Groove aspect ratio” indicates a value obtained by dividing D by W. “Si etching amount” indicates a value E1 obtained by subtracting the thickness of the single crystal silicon substrate subjected to dry etching from the thickness (original thickness) of the single crystal silicon substrate before dry etching is performed. “SD etching amount” indicates a value E2 obtained by adding D to E1. “Etching time” indicates a time T in which dry etching has been performed. “Si etching rate” indicates a value obtained by dividing E1 by T. “SD etching rate” indicates a value obtained by dividing E2 by T. “Etching rate ratio” indicates a value obtained by dividing E2 by E1.

The followings are understood from the results of the first experiment illustrated in FIG. 12. That is, if the fracture reaches one surface (one surface in a case where dry etching is performed on the single crystal silicon substrate from the one surface side), dry etching progresses selectively (that is, at a high etching rate ratio) from the one surface side along the fracture within a range in which fractures are connected to each other. Thus, a groove having an opening which is narrow in width and is deep (that is, the groove aspect ratio is high) is formed (comparison of “VL pattern processing surface: ST” and “VL pattern processing surface: ablation” to “standard processing surface: HC”). The fracture significantly contributes to selective progress of dry etching more than the modified region itself (comparison of “VL pattern processing surface: HC” and “VL pattern processing surface: ablation” to “standard processing surface: HC”). If the fractures extending from the modified regions in the thickness direction are not connected to each other, selective progress of dry etching is stopped at a portion (black streak portion viewed in (a) in FIG. 11) in which the fractures are not connected to each other (comparison of “tact-up processing surface: HC” to “standard processing surface: HC”). Stopping the selective progress of dry etching means that a progress speed of dry etching decreases.

In a second experiment (see FIGS. 14 and 15), a plurality of lines to cut was set in stripes on a single crystal silicon substrate having a thickness of 100 μm, at an interval of 100 μm. Then, two rows of modified regions arranged in a thickness direction of the single crystal silicon substrate were formed in the single crystal silicon substrate along each of the plurality of lines to cut. Here, a state where the modified regions adjacent to each other in the thickness direction are separated from each other, and fractures extending from the modified regions in the thickness direction reach both one surface and the other surface (surface on an opposite side of the one surface) occurred. Reactive ion etching with CF₄ was performed on the one surface of the single crystal silicon substrate.

FIGS. 14 and 15 illustrate results of the second experiment. In FIGS. 14 and 15, “CF₄: 60 min” indicates a case where reactive ion etching with CF₄ was performed for 60 minutes. “CF₄: 120 min” indicates a case where reactive ion etching with CF₄ was performed for 120 minutes. (a) in FIG. 14 is a plan picture (picture of the one surface) of the single crystal silicon substrate before reactive ion etching is performed. (b) in FIG. 14 is a bottom picture (picture of the other surface) of the single crystal silicon substrate after reactive ion etching is performed. (a) in FIG. 15 is a side picture of a single crystal silicon chip obtained by cutting the single crystal silicon substrate along each of the plurality of lines to cut. (b) FIG. 15 is a diagram illustrating dimensions of the single crystal silicon chip. In (a) and (b) in FIG. 15, the one surface of the single crystal silicon substrate is on the lower side.

The followings are understood from the results of the second experiment illustrated in FIGS. 14 and 15. That is, if the fracture reaches one surface (one surface in a case where dry etching is performed on the single crystal silicon substrate from the one surface side), dry etching progresses selectively (that is, at a high etching rate ratio) from the one surface side along the fracture within a range in which fractures are connected to each other. Thus, a groove having an opening which is narrow in width and is deep (that is, the groove aspect ratio is high) is formed. If fractures extending from the modified regions in the thickness direction reach both one surface and the other surface, it is possible to completely chip the single crystal silicon substrate only by dry etching. If an extension film stuck to the other surface of the single crystal silicon substrate is extended in a case of “CF₄: 60 min”, it is possible to cut the single crystal silicon substrate having a rectangular shape of 50 mm×50 mm into chips of 100 μm×100 μm at a ratio of 100%.

In a third experiment (see FIG. 16), a plurality of lines to cut was set in stripes on a single crystal silicon substrate having a thickness of 400 μm, at an interval of 2 mm. Then, a plurality of rows of modified regions arranged in a thickness direction of the single crystal silicon substrate was formed in the single crystal silicon substrate along each of the plurality of lines to cut. A state where one row of modified regions on one surface side is separated from the one surface, and a fracture reaches the one surface from the one row of modified regions, in a case where laser light is converged by natural spherical aberration, and a state where fractures extending from the modified regions in the thickness direction are connected to each other occurred. Reactive ion etching was performed on the one surface of the single crystal silicon substrate.

FIG. 16 illustrates results of the third experiment. In FIG. 16, “CF₄ (RIE)” indicates a case where reactive ion etching with CF₄ was performed by a reactive ion etching (RIE) apparatus, “SF₆ (RIE)” indicates a case where reactive ion etching with sulfur hexafluoride (SF₆) was performed by a RIE apparatus, and “SF₆ (DRIE)” indicates a case where reactive ion etching with SF₆ was performed by a deep reactive ion etching (DRIE) apparatus. (a) in FIG. 16 is a plan picture of the single crystal silicon substrate after reactive ion etching is performed. (b) in FIG. 16 is a section picture (picture of a cut surface perpendicular to the line to cut) of the single crystal silicon substrate after reactive ion etching is performed.

The followings are understood from the results of the third experiment illustrated in FIG. 16. That is, even though reactive ion etching with CF₄ requires longer time than reactive ion etching with SF₆, from a point that it is possible to ensure a high etching rate ratio and a high groove aspect ratio, reactive ion etching with CF₄ is more advantageous than reactive ion etching with SF₆, for ensuring the uniform Si etching amount.

In a fourth experiment (see FIG. 17), a plurality of lines to cut was set in stripes on a single crystal silicon substrate having a thickness of 400 at an interval of 2 mm. Then, a plurality of rows of modified regions arranged in a thickness direction of the single crystal silicon substrate was formed in the single crystal silicon substrate along each of the plurality of lines to cut. In FIG. 17, “CF₄ (RIE): 30 min, surface: HC”, “CF₄ (RIE): 60 min, surface: HC”, and “CF₄ (RIE): 6 H, surface: HC” mean a state where one row of modified regions on one surface side is separated from the one surface, and a fracture reaches the one surface from the one row of modified regions, in a case where laser light is converged by natural spherical aberration, and a state where fractures extending from the modified regions in the thickness direction are connected to each other. “CF₄ (RIE): 6 H, surface: ST” means a state where one row of modified regions on one surface side is separated from the one surface, and a fracture does not reach the one surface from the one row of modified regions, in a case where laser light is converged by natural spherical aberration, and a state where fractures extending from the modified regions in the thickness direction are connected to each other.

Reactive ion etching with CF₄ was performed on the one surface of the single crystal silicon substrate. In FIG. 17, “CF₄ (RIE): 30 min, surface: HC”, “CF₄ (RIE): 60 min, surface: HC”, “CF₄ (RIE): 6 H, surface: HC”, and “CF₄ (RIE): 6 H, surface: ST” mean that reactive ion etching with CF₄ was performed for 30 minutes, 60 minutes, 6 hours, and 6 hours, respectively, by the RIB apparatus.

FIG. 17 illustrates results of the fourth experiment. (a) in FIG. 17 is a section picture (picture of a cut surface perpendicular to the line to cut) of the single crystal silicon substrate after reactive ion etching is performed.

The followings are understood from the results of the fourth experiment illustrated in FIG. 17. That is, if the fracture reaches one surface (one surface in a case where dry etching is performed on the single crystal silicon substrate from the one surface side), selective progress of dry etching does not stop (that is, a high etching rate ratio is maintained) in a range in which fractures are connected to each other. Even though the fracture does not reach the one surface, etching from the one surface is in progress. If the fracture appears to the one surface, selective progress of dry etching starts along the fracture. Since it is difficult to stop extension of the fracture at a predetermined depth from the one surface, a timing at the fracture appears to the one surface by the progress of etching varies easily depending on a place. As a result, the width and the depth of an opening of a groove to be formed vary easily depending on the place. Thus, when one row of modified regions on one surface side is formed, it is very important to form the modified regions such that a fracture reaches the one surface.

In a fifth experiment (see FIG. 18), a plurality of lines to cut was set in grid on a single crystal silicon substrate having a thickness of 320 μm, at an interval of 3 mm. Then, a plurality of rows of modified regions arranged in a thickness direction of the single crystal silicon substrate was formed in the single crystal silicon substrate along each of the plurality of lines to cut. A state where one row of modified regions on one surface side is separated from the one surface, and a fracture reaches the one surface from the one row of modified regions, in a case where laser light is converged by natural spherical aberration, and a state where fractures extending from the modified regions in the thickness direction are connected to each other occurred.

Reactive ion etching was performed on the one surface of the single crystal silicon substrate. In FIG. 18, “CF₄ (RIE), surface: HC” means that reactive ion etching with CF₄ was performed by a RIE apparatus. “XeF₂, surface: HC” means that reactive gas etching with xenon difluoride (XeF₂) was performed by a sacrificial layer etcher apparatus. “XeF₂, surface: HC, SiO₂ etching protection layer” means that reactive gas etching with XeF₂ was performed by a sacrificial layer etcher apparatus in a state where an etching protection layer made of silicon dioxide (SiO₂) was formed on one surface of the single crystal silicon substrate, and a fracture reaches a surface (outer surface on an opposite side of the single crystal silicon substrate) of the etching protection layer from one row of modified regions on the one surface side.

FIG. 18 illustrates results of the fifth experiment. (a) in FIG. 18 is a plan picture of the single crystal silicon substrate before reactive ion etching is performed. (b) in FIG. 18 is a plan picture of the single crystal silicon substrate after reactive ion etching is performed. (c) in FIG. 18 is a section picture (picture of a cut surface perpendicular to the line to cut) of the single crystal silicon substrate after reactive ion etching is performed. A removal width is a width of an opening on the other surface of the single crystal silicon substrate in a case where the groove reaches the other surface.

The followings are understood from the results of the fifth experiment illustrated in FIG. 18. That is, if the etching protection layer made of SiO₂ is not formed on one surface of the single crystal silicon substrate (the one surface in a case where dry etching is performed on the single crystal silicon substrate from the one surface side), a difference between reactive ion etching with CF₄ and reactive gas etching with XeF₂ is not large from a point of ensuring a high etching rate ratio and a high groove aspect ratio. If the etching protection layer made of SiO₂ is formed on the one surface of the single crystal silicon substrate, and the fracture reaches the surface of the etching protection layer from one row of modified regions on the one surface side, the etching rate ratio and the groove aspect ratio increase significantly.

In a sixth experiment (see FIG. 19), a plurality of lines to cut was set in grid on a single crystal silicon substrate which has a thickness of 320 μm and in which an etching protection layer made of SiO₂ is formed on one surface, at an interval of 3 mm. Then, a plurality of rows of modified regions arranged in a thickness direction of the single crystal silicon substrate was formed in the single crystal silicon substrate along each of the plurality of lines to cut. Reactive gas etching with XeF₂ was performed on the one surface of the single crystal silicon substrate by a sacrificial layer etcher apparatus for 180 minutes.

In FIG. 19, “standard processing, surface: HC” means a state where the modified regions adjacent to each other in the thickness direction are separated from each other, one row of modified regions on one surface side is separated from the one surface, and a fracture reaches a surface (outer surface on an opposite side of the single crystal silicon substrate) of the etching protection layer from the one row of modified regions, and a state where fractures extending from the modified regions in the thickness direction are connected to each other. “Standard processing, surface: ST” means a state where the modified regions adjacent to each other in the thickness direction are separated from each other, one row of modified regions on the one surface side is separated from the one surface, and a fracture does not reach the one surface from the one row of modified regions, and a state where fractures extending from the modified regions in the thickness direction are connected to each other.

“Tact-up processing 1, surface: HC” means a state where the modified regions adjacent to each other in the thickness direction are separated from each other, one row of modified regions on the one surface side is separated from the one surface, and a fracture reaches the surface of the etching protection layer from the one row of modified regions, and a state where fractures extending from the modified regions in the thickness direction are connected to each other. “Tact-up processing 2, surface: HC” means a state where the modified regions adjacent to each other in the thickness direction are separated from each other, one row of modified regions on the one surface side is separated from the one surface, and a fracture reaches the surface of the etching protection layer from the one row of modified regions, and a state where some of fractures extending from the modified regions in the thickness direction are connected to each other.

“VL pattern processing, surface: HC” means a state where the modified regions adjacent to each other in the thickness direction are connected to each other, one row of modified regions on the one surface side is separated from the one surface, and a fracture reaches the surface of the etching protection layer from the one row of modified regions. “VL pattern processing, surface: ablation” means a state where the modified regions adjacent to each other in the thickness direction are connected to each other, and the one row of modified regions on the one surface side is exposed to the surface of the etching protection layer.

FIG. 19 illustrates results of the sixth experiment. (a) in FIG. 19 is a section picture (picture of a cut surface perpendicular to the line to cut) of the single crystal silicon substrate after reactive ion etching is performed. (b) in FIG. 19 is a picture of a cut surface of the single crystal silicon substrate after reactive ion etching is performed.

The followings are understood from the results of the fifth experiment illustrated in FIG. 19. That is, if the fracture reaches the surface of the etching protection layer, dry etching progresses selectively (that is, at a high etching rate ratio) from the one surface side along the fracture within a range in which fractures are connected to each other. Thus, a groove having an opening which is narrow in width and is deep (that is, the groove aspect ratio is high) is formed. If the fractures extending from the modified regions in the thickness direction are not connected to each other, dry etching progresses isotropically at a portion in which the fractures are not connected to each other (picture of the (a) field in “tact-up processing 2, surface: HC”.

The followings are understood from the experimental results on the above-described object cutting methods. That is, presuming that the fracture reaches the one surface from one row of modified regions on the one surface side (one surface in a case where dry etching is performed on the single crystal silicon substrate from the one surface side) (in a case where the etching protection layer made of SiO₂ is formed on the one surface of the single crystal silicon substrate, the fracture reaches the surface of the etching protection layer), within a range in which fractures are connected to each other, as illustrated in FIG. 20, reactive ion etching with CF₄ and reactive gas etching with XeF₂ can ensure a high reactive gas etching rather than reactive ion etching with SF₆. Further, if the etching protection layer made of SiO₂ is formed on the one surface of the single crystal silicon substrate, and the fracture reaches the surface of the etching protection layer from one row of modified regions on the one surface side, the etching rate ratio increases significantly. Focusing on the groove aspect ratio, reactive ion etching with CF₄ is particularly excellent. Reactive gas etching with XeF₂ is advantageous from a point of preventing the decrease of strength of the single crystal silicon substrate by plasma.

The principle in which dry etching selectively progresses along a fracture will be explained. If the converging point P of laser light L oscillating in a pulsating manner is located in the object 1, and the converging point P is relatively moved along the line 5 to cut, as illustrated in FIG. 21, a plurality of modified spots 7 a arranged along the line 5 to cut is formed in the object 1. The plurality of modified spots 7 a arranged along the line 5 to cut corresponds to one row of modified regions 7.

In a case where a plurality of rows of modified regions 7 arranged in the thickness direction of the object 1 is formed in the object 1, if a fracture 31 is formed to extend between the second main surface 1 b and one row of modified regions 7 on the second main surface 1 b (second main surface 1 b in a case where dry etching is performed on the object 1 from the second main surface 1 b side) side of the object 1, an etching gas enters into fractures 31 having intervals of several nm to several μm, in a manner as with capillarity (see an arrow in FIG. 21). Thus, it is supposed that dry etching selectively progresses along the fracture 31.

From this, if the fracture 31 is formed to extend between the modified regions 7 adjacent to each other among the plurality of rows of modified regions 7, it is supposed that dry etching selectively progresses deeper. Further, if the fracture 31 is formed to extend between the modified spots 7 a adjacent to each other among the plurality of modified spots 7 a arranged along the line 5 to cut, it is supposed that dry etching selectively progresses with higher efficiency. At this time, the etching gas comes into contact with each of the modified spots 7 a from the surroundings of the modified spot 7 a. Thus, it is supposed that the modified spot 7 a having a size of about several μm is removed quickly.

Here, the fracture 31 is different from microcracks included in each modified spot 7 a, microcracks randomly formed around each modified spot 7 a, and the like. Here, the fracture 31 is a fracture which is parallel to the thickness direction of the object 1 and extends along a plane including the line 5 to cut. In a case where the fracture 31 herein is formed in the single crystal silicon substrate, surfaces (fracture surface facing each other at a distance of several nm to several μm) formed by the fracture 31 are surfaces on which single crystal silicon is exposed. The modified spot 7 a formed in the single crystal silicon substrate includes a polycrystalline silicon region, a high dislocation density region, and the like.

First Embodiment

An object cutting method according to a first embodiment will be explained. Constituents illustrated in FIGS. 22 to 26 and FIGS. 28 to 38 are schematic, and an aspect ratio and the like of each constituent are different from those of the practical one. Firstly, as a first step, as illustrated in FIG. 22(a), an object to be processed 1 including a single crystal silicon substrate 11 and a functional device layer 12 provided on a first main surface 1 a side is prepared, and a protective film 21 is stuck to the first main surface 1 a of the object 1. Then, an etching protection layer 23 made of SiO₂ is formed on a second main surface 1 b of the object 1 by vapor deposition, for example. SiO₂ is a material having transparency to laser light L.

After the first step, as a second step, as illustrated in FIG. 22(b), if the object 1 is irradiated with laser light L through the etching protection layer 23, a plurality of rows of modified regions 7 is formed in the single crystal silicon substrate 11 along each of a plurality of lines 5 to cut, and a fracture 31 is formed in the object 1 along each of the plurality of lines 5 to cut. A plurality of rows of modified regions 7 formed along each of the plurality of lines 5 to cut is arranged in the thickness direction of the object 1. Each of the plurality of rows of modified regions 7 is constituted by a plurality of modified spots 7 a arranged along the line 5 to cut (see FIG. 21). The fracture 31 extends between one row of modified regions 7 on the second main surface 1 b side and a surface 23 a (outer surface on an opposite side of the single crystal silicon substrate 11) of the etching protection layer 23, and between the modified regions 7 adjacent to each other among the plurality of rows of modified regions 7. Further, the fracture 31 extends between the modified spots 7 a adjacent to each other among the plurality of modified spots 7 a (see FIG. 21). Here, the fracture 31 formed in the etching protection layer 23 along each of the plurality of lines 5 to cut functions as a gas passage region in the etching protection layer 23.

After the second step, as a third step, as illustrated in FIG. 23(a), dry etching is performed on the object 1 from the second main surface 1 b side in a state where the etching protection layer 23 is formed on the second main surface 1 b, and thereby a groove 32 is formed in the object 1 along each of the plurality of lines 5 to cut, as illustrated in FIG. 23(b).

The groove 32 is, for example, a V groove (groove having a V-shaped section) opening to the second main surface 1 b. Here, dry etching is performed on the object 1 from the second main surface 1 b side with XeF₂ (that is, reactive gas etching with XeF₂ is performed). Here, dry etching is performed on the object 1 from the second main surface 1 b side such that the etching protection layer 23 remains. Further, here, the dry etching is performed on the object 1 from the second main surface 1 b such that one row of modified regions 7 on the second main surface 1 b side among the plurality of rows of modified regions 7 is removed, and thereby an uneven region 9 having an uneven shape corresponding to the one removed row of modified regions 7 is formed in the inner surface of the groove 32. In a case of forming the uneven region 9, dry etching is preferably performed until the modified region 7 (modified spot 7 a) is completely removed from the inner surface of the groove 32. Preferably, dry etching is not performed until the uneven region 9 is completely removed.

After the third step, as a fourth step, as illustrated in FIG. 24(a), an extension film 22 is stuck to a surface 23 a of the etching protection layer 23 (that is, stuck to the second main surface 1 b side of the object 1), and, as illustrated in FIG. 24(b), the protective film 21 is removed from the first main surface 1 a of the object 1. As illustrated in FIG. 25(a), if the extension film 22 is extended, the object 1 is cut into a plurality of semiconductor chips 15 along each of the plurality of lines 5 to cut. Then, as illustrated in FIG. 25(b), the semiconductor chips 15 are picked up.

The semiconductor chip 15 obtained by the object cutting method according to the first embodiment as described above will be explained. As illustrated in FIG. 26, the semiconductor chip 15 includes a single crystal silicon substrate 110, a functional device layer 120 provided on a first surface 110 a side of the single crystal silicon substrate 110, and an etching protection layer 230 formed on a second surface 110 b (surface on an opposite side of the first surface 110 a) of the single crystal silicon substrate 110. The single crystal silicon substrate 110 is a portion cut out from the single crystal silicon substrate 11 of the object 1 (see FIG. 25). The functional device layer 120 is a portion cut out from the functional device layer 12 of the object 1 (see FIG. 25) and includes one functional device 12 a. The etching protection layer 230 is a portion cut out from the etching protection layer 23 (see FIG. 25).

The single crystal silicon substrate 110 includes a first portion 111 and a second portion (portion) 112. The first portion 111 is a portion on the first surface 110 a side. The second portion 112 is a portion on the second surface 110 b side. The second portion 112 has a shape which becomes thinner as becoming farther from the first surface 110 a. The second portion 112 corresponds to a portion at which the groove 32 is formed in the single crystal silicon substrate 11 of the object 1 (that is, a portion at which dry etching has progressed) (see FIG. 25). As an example, the first portion 111 has a quadrangular plate shape (rectangular parallelepiped shape). The second portion 112 has a quadrangular pyramid shape which becomes thinner as becoming farther from the first portion 111.

A modified region 7 is formed in the side surface 111 a of the first portion 111 to have a band shape. That is, the modified region 7 extends in a direction parallel to the first surface 110 a along each side surface 111 a, in each side surface 111 a. The modified region 7 on the first surface 110 a side is separated from the first surface 110 a. The modified region 7 is constituted by a plurality of modified spots 7 a (see FIG. 21). The plurality of modified spots 7 a is arranged in the direction parallel to the first surface 110 a along each side surface 111 a, in each side surface 111 a. The modified region 7 (more specifically, each modified spot 7 a) includes a polycrystalline silicon region, a high dislocation density region, and the like.

An uneven region 9 is formed in the side surface 112 a of the second portion 112 to have a band shape. That is, the uneven region 9 extends in a direction parallel to the second surface 110 b along each side surface 112 a, in each side surface 112 a. The uneven region 9 on the second surface 110 b side is separated from the second surface 110 b. The uneven region 9 is formed by removing the modified region 7 on the second main surface 1 b side of the object 1 by dry etching (see FIG. 25). Thus, the uneven region 9 has an uneven shape corresponding to the modified region 7, and single crystal silicon is exposed in the uneven region 9. That is, the side surface 112 a of the second portion 112 serves as a surface which includes an uneven surface of the uneven region 9 and in which single crystal silicon is exposed.

The semiconductor chip 15 may not include the etching protection layer 230. Such a semiconductor chip 15 is obtained, for example, in a case where dry etching is performed from the second main surface 1 b side to remove the etching protection layer 23.

In FIG. 27(a), an upper part is a picture of the uneven region 9, and a lower part is an uneven profile of the uneven region 9 along a one-dot chain line at the upper part. In FIG. 27(b), an upper part is a picture of the modified region 7, and a lower part is an uneven profile of the modified region 7 along a one-dot chain line at the upper part. Comparing the drawings, it is understood that there is a tendency in which only a plurality of relatively large recessed portions is formed in the uneven region 9, but there is a tendency in which a plurality of relatively large protrusion portions and the plurality of relatively large recessed portions are randomly formed in the modified region 7. FIG. 27(c) is a picture and an uneven profile of “the modified region 7 on the second main surface 1 b side” in a case where the object 1 has been cut without performing dry etching on the object 1 from the second main surface 1 b side. In the modified region 7 in this case, there is also a tendency in which a plurality of relatively large protrusion portions is randomly formed in addition to the plurality of relatively large recessed portions. That is, it is understood that a tendency in which only a plurality of relatively large recessed portions is formed in the uneven region 9 is caused by removing the modified region 7 by dry etching.

As described above, according to the first embodiment, the object cutting method includes the first step of preparing the object 1 including the single crystal silicon substrate 11 and the functional device layer 12 provided on the first main surface 1 a side, the second step of irradiating the object 1 with laser light L to form at least one row of modified regions 7 in the single crystal silicon substrate 11 along each of the plurality of lines 5 to cut and to form the fracture 31 in the object 1 so as to extend between the at least one row of modified regions 7 and the second main surface 1 b of the object 1 along each of the plurality of lines 5 to cut, and the third step of, after the second step, performing dry etching on the object 1 from the second main surface 1 b side to form the groove 32 opening to the second main surface 1 b, in the object 1 along each of the plurality of lines 5 to cut.

In the object cutting method, the dry etching is performed from the second main surface 1 b side, on the object 1 in which the fracture 31 is formed to extend between the at least one row of modified regions 7 and the second main surface 1 b of the object 1. Thus, the dry etching selectively progresses from the second main surface 1 b along the fracture 31, and the groove 32 in which an opening is narrow in width and deep is formed along each of the plurality of lines 5 to cut. Thus, it is possible to reliably cut the object 1 into the plurality of semiconductor chips 15 along each of the lines 5 to cut, by extending the extension film 22 stuck to the second main surface 1 b side to which the groove 32 opens, for example.

In the third step, dry etching is performed from the second main surface 1 b such that the at least one row of modified regions 7 is removed, and the uneven region which has an uneven shape corresponding to the removed modified region 7 and in which single crystal silicon is exposed is formed in the inner surface of the groove 32. Thus, since the uneven region 9 in which single crystal silicon is exposed is formed, it is possible to suppress a decrease of strength in the vicinity of the uneven region 9.

In the third step, dry etching is performed with XeF₂ from the second main surface 1 b, in a state where the etching protection layer 23 in which the gas passage region (Here, fracture 31) is formed along each of the plurality of lines to cut is formed on the second main surface 1 b. Accordingly, it is possible to cause dry etching to selectively progress with higher efficiency and to form the groove 32 having an opening which is narrow in width and is deep, with higher efficiency.

In particular, since the fracture 31 is formed to extend between the at least one row of modified regions 7 and the surface 23 a of the etching protection layer 23, it is possible to save labor, for example, for forming a slit in the etching protection layer 23 by performing patterning on the etching protection layer 23.

In the third step, dry etching is performed from the second main surface 1 b side such that the etching protection layer 23 remains. Thus, it is possible to cause the etching protection layer 23 to function as a strong reinforcing layer or a gettering layer for capturing impurities, in the semiconductor chip 15. Further, it is possible to maintain the original thickness of the single crystal silicon substrate 11, in the semiconductor chip 15. In the third step, dry etching may be performed from the second main surface 1 b side to remove the etching protection layer 23. According to this configuration, it is possible to prevent an occurrence of an unnecessary influence by the etching protection layer 23, in the semiconductor chip 15.

In the first step, the etching protection layer 23 is formed with a material having transparency to laser light L. In the second step, the object 1 is irradiated with the laser light L through the etching protection layer 23. Thus, it is possible to enter the laser light L into the single crystal silicon substrate 11 from an opposite side of the functional device layer 12. Accordingly, it is possible to reliably form the modified region 7 and the fracture 31 regardless of the configuration of the functional device layer 12.

In the second step, since the plurality of rows of modified regions 7 arranged in the thickness direction of the object 1 is formed, at least one row of modified regions 7 is formed along each of the plurality of lines 5 to cut, and the fracture 31 is formed to extend between the modified regions 7 adjacent to each other among the plurality of rows of modified regions 7. Thus, it is possible to cause dry etching to selectively progress deeper. In this case, in the third step, dry etching is performed from the second main surface 1 b side such that modified regions 7 on the second main surface 1 b side among the plurality of rows of modified regions 7 are removed, and thereby the uneven region 9 having an uneven shape corresponding to the removed modified region 7 is formed in the inner surface of the groove 32.

In the second step, the at least one row of modified regions 7 may be formed along each of the plurality of lines 5 to cut by forming the plurality of modified spots 7 a arranged along each of the plurality of lines 5 to cut, and the fracture 31 may be formed to extend between modified spots 7 a adjacent to each other among the plurality of rows of modified spots 7 a. Thus, it is possible to cause the dry etching to selectively progress with higher efficiency.

In the fourth step, the object 1 is cut into the plurality of semiconductor chips 15 along each of the plurality of lines 5 to cut by sticking the extension film 22 to the second main surface 1 b side and extending the extension film 22. Thus, it is possible to reliably cut the object 1 into the plurality of semiconductor chips 15 along each of the lines 5 to cut. Further, since the plurality of semiconductor chips 15 is spaced from each other on the extension film 22, it is possible to easily pick the semiconductor chips 15 up.

The semiconductor chip 15 includes the single crystal silicon substrate 110 and the functional device layer 120 provided on the first surface 110 a side of the single crystal silicon substrate 110. The second portion 112 on at least the second surface 110 b side in the single crystal silicon substrate 110 has a shape which becomes thinner as becoming farther from the first surface 110 a. The uneven region 9 which has an uneven shape and in which single crystal silicon is exposed is formed in the side surface 112 a of the second portion 112 to have a band shape.

In the semiconductor chip 15, it is possible to cause the uneven region 9 to function as a gettering region of capturing impurities. Since single crystal silicon is exposed in the uneven region 9, it is possible to suppress the decrease of strength in the vicinity of the uneven region 9.

For example, a pressure-sensitive tape having vacuum resistance, a UV tape, or the like can be used as the protective film 21. Instead of the protective film 21, a wafer fixing jig having etching resistance may be used.

The material of the etching protection layer 23 is not limited to SiO₂ so long as the material has transparency to laser light L. As the etching protection layer 23, for example, a resist film or a resin film may be formed on the second main surface 1 b of the object 1 by spin coating, or a sheet-like member (transparent resin film and the like) and a rear-surface protection tape (IRLC tape/WP tape) may stick to the second main surface 1 b of the object 1.

The gas passage region formed in the etching protection layer 23 along each of the plurality of lines 5 to cut is not limited to the fracture 31. As the gas passage region, for example, a slit for exposing the second main surface 1 b of the object 1 may be formed by performing patterning on the etching protection layer 23, or a modified region (region including multiple microcracks, ablation region, and the like) may be formed by performing irradiation with laser light L.

The number of rows of modified regions 7 formed in the single crystal silicon substrate 11 along each of the plurality of lines 5 to cut is not limited to a plurality of rows and may be one row. That is, at least one row of modified regions 7 may be formed in the single crystal silicon substrate 11 along each of the plurality of lines 5 to cut. In a case where a plurality of rows of modified regions 7 is formed in the single crystal silicon substrate 11 along each of the plurality of lines 5 to cut, the modified regions 7 adjacent to each other may be connected to each other.

The fracture 31 may be formed to extend between at least one row of modified regions 7 and the second main surface 1 b of the object 1. That is, the fracture 31 may not reach the second main surface 1 b if the fracture is partial. Further, if the fracture 31 is partial, the fracture 31 may not extend between the modified regions 7 adjacent to each other and may not extend between the modified spots 7 a adjacent to each other. The fracture 31 may or may not reach the first main surface 1 a of the object 1.

Dry etching may be performed from the second main surface 1 b side to remove the etching protection layer 23. Dry etching may be performed from the second main surface 1 b side such that the plurality of rows of modified regions 7 is removed, and thereby the uneven region 9 which has an uneven shape corresponding to the plurality of rows of removed modified regions 7 and in which single crystal silicon is exposed is Banned in the inner surface of the groove 32. The type of dry etching is not limited to reactive gas etching with XeF₂. As dry etching, for example, reactive ion etching with CF₄ or reactive ion etching with SF₆ may be performed.

In a case where the plurality of rows of modified regions 7 is formed in the single crystal silicon substrate 11 along each of the plurality of lines 5 to cut, dry etching may be performed, as illustrated in FIG. 28(a), such that the etching protection layer 23 remains, and some modified regions 7 are removed. Alternatively, thy etching may be performed such that the etching protection layer 23 remains, and all the modified regions 7 are removed, as illustrated in FIG. 28(b). Alternatively, dry etching may be performed such that the etching protection layer 23 remains, and the object 1 is completely divided, as illustrated in FIG. 28(c).

In a case where the plurality of rows of modified regions 7 is formed in the single crystal silicon substrate 11 along each of the plurality of lines 5 to cut, dry etching may be performed, as illustrated in FIG. 29(a), such that the etching protection layer 23 remains, and the sectional shape of the groove 32 has a U-shape. Alternatively, dry etching may be performed such that the etching protection layer 23 remains, and the sectional shape of the groove 32 has an I-shape, as illustrated in FIG. 29(b).

In a case where the plurality of rows of modified regions 7 is formed in the single crystal silicon substrate 11 along each of the plurality of lines 5 to cut, dry etching may be performed, as illustrated in FIG. 30(a), such that the etching protection layer 23 is removed, and some modified regions 7 are removed. Alternatively, dry etching may be performed such that the etching protection layer 23 is removed, and all the modified regions 7 are removed, as illustrated in FIG. 30(b).

Alternatively, dry etching may be performed such that the etching protection layer 23 is removed, and the object 1 is completely divided, as illustrated in FIG. 30(c).

In a case where the plurality of rows of modified regions 7 is formed in the single crystal silicon substrate 11 along each of the plurality of lines 5 to cut, dry etching may be performed, as illustrated in FIG. 31(a), such that the etching protection layer 23 is removed, and the sectional shape of the groove 32 has a U-shape. Alternatively, dry etching may be performed such that the etching protection layer 23 is removed, and the sectional shape of the groove 32 has an I-shape, as illustrated in FIG. 31(b).

In a case where dry etching is performed such that the object 1 is completely divided (see FIGS. 28(c), 29(b), 30(c), and 31(b)), it is not necessary that the extension film 22 is extended. However, in order to easily pick the semiconductor chip 15 up, the extension film 22 may be extended, and thus the plurality of semiconductor chips 15 on the extension film 22 may be spaced from each other.

In the semiconductor chip 15, as illustrated in FIG. 32, at least one row of uneven regions 9 may be formed to have a band shape in the side surface 110 c of the single crystal silicon substrate 110, without the modified region 7 remaining. The uneven region 9 is formed by removing all of the modified regions 7 formed in the single crystal silicon substrate 11 of the object 1 by dry etching (see FIGS. 30(b) and 30(c)). Such a semiconductor chip 15 is obtained, for example, in a case where dry etching is performed from the second main surface 1 b to completely divide the object 1. In the semiconductor chip 15 illustrated in FIG. 32, the entirety of the single crystal silicon substrate 110 has a shape which becomes thinner as becoming farther from the first surface 110 a. That is, the entirety of the side surface 110 c of the single crystal silicon substrate 110 corresponds to the inner surface of the groove 32 formed in the single crystal silicon substrate 11 of the object 1 (see FIGS. 30(b) and 30(c)). As an example, the entirety of the single crystal silicon substrate 110 has a quadrangular pyramid shape which becomes thinner as becoming farther from the first surface 110 a. The semiconductor chip 15 illustrated in FIG. 32 may include the etching protection layer 230 formed on the second surface 110 b of the single crystal silicon substrate 110.

A first step and a second step as follows may be performed instead of the first step and the second step described above. That is, as the first step, as illustrated in FIG. 33(a), an object to be processed 1 is prepared, and an etching protection layer 23 is formed on a second main surface 1 b of the object 1. In this case, it is not necessary that the material of the etching protection layer 23 is a material having transparency to laser light L. As illustrated in FIG. 33(b), a protective film 21 is stuck to a surface 23 a of the etching protection layer 23. After the first step, as a second step, as illustrated in FIG. 34(a), if the object 1 is irradiated with laser light L by using a first main surface 1 a as a laser light entrance surface, at least one row of modified regions 7 is formed in the single crystal silicon substrate 11 along each of a plurality of lines 5 to cut, and a fracture 31 is formed in the object 1 along each of the plurality of lines 5 to cut, so as to extend between the at least one row of modified regions 7 and the surface 23 a of the etching protection layer 23. As illustrated in FIG. 34(b), another protective film 21 is stuck to the first main surface 1 a, and the protective film 21 which has been previously stuck is removed from the surface 23 a of the etching protection layer 23. The subsequent steps are similar to the steps subsequent to the third step described above.

In a case where the material of the protective film 21 stuck to the first main surface 1 a of the object 1 is a material having transparency to laser light L, the object 1 may be irradiated with the laser light L through the protective film 21, as illustrated in FIG. 35.

An object cutting method as follows can be performed. With the object cutting method as follows, it is also possible to reliably cut the object 1 into a plurality of semiconductor chips 15.

Firstly, as a first step, as illustrated in FIG. 36(a), an object to be processed 1 including a single crystal silicon substrate 11 and a functional device layer 12 provided on a first main surface 1 a side is prepared, and a protective film 21 is stuck to a second main surface 1 b of the object 1. An etching protection layer 23 is formed on the first main surface 1 a of the object 1. The material of the etching protection layer 23 is a material having transparency to laser light L. A passivation film provided on the functional device layer 12 may be used as the etching protection layer 23.

After the first step, as a second step, as illustrated in FIG. 36(b), if the object 1 is irradiated with laser light L through the etching protection layer 23, at least one row of modified regions 7 is formed in the single crystal silicon substrate 11 along each of a plurality of lines 5 to cut, and a fracture 31 is formed in the object 1 along each of the plurality of lines 5 to cut, so as to extend between the at least one row of modified regions 7 and the surface 23 a of the etching protection layer 23. Here, the fracture 31 formed in the etching protection layer 23 along each of the plurality of lines 5 to cut functions as a gas passage region in the etching protection layer 23.

After the second step, as a third step, as illustrated in FIG. 37(a), dry etching is performed on the object 1 from the first main surface 1 a side in a state where the etching protection layer 23 is formed on the first main surface 1 a, and thereby a groove 32 is formed in the object 1 along each of the plurality of lines 5 to cut, as illustrated in FIG. 37(b).

The groove 32 is, for example, a V groove (groove having a V-shaped section) opening to the first main surface 1 a. Here, dry etching is performed on the object 1 from the first main surface 1 a side such that the etching protection layer 23 remains. However, dry etching may be performed on the object 1 from the first main surface 1 a side to remove the etching protection layer 23.

Performing dry etching on the object 1 from the first main surface 1 a side has the meaning that dry etching is performed on the single crystal silicon substrate 11 in a state where the second main surface 1 b is covered with the protective film and the like, and the first main surface 1 a (or etching protection layer 23 in which a gas passage region is formed along each of the plurality of lines 5 to cut) is exposed to an etching gas. In particular, in a case of performing reactive ion etching (plasma etching), performing dry etching means irradiation of the first main surface 1 a (or etching protection layer 23 in which the gas passage region is formed along each of the plurality of lines 5 to cut) with reactive species in plasma.

After the third step, as a fourth step, as illustrated in FIG. 38(a), the object 1 is cut into a plurality of semiconductor chips 15 along each of the plurality of lines 5 to cut by extending the protective film 21 stuck to the second main surface 1 b of the object 1, as the extension film 22. Then, as illustrated in FIG. 38(b), the semiconductor chips 15 are picked up.

Second Embodiment

An object cutting method according to a second embodiment will be explained. Constituents illustrated in FIGS. 39 to 42 are schematic, and an aspect ratio and the like of each constituent are different from those of the practical one. Firstly, as a first step, as illustrated in FIG. 39(a), an object to be processed 1 including a single crystal silicon substrate 11 and a functional device layer 12 provided on a first main surface 1 a side is prepared, and a protective film 21 is stuck to a first main surface 1 a of the object 1.

After the first step, as a second step, the object 1 is irradiated with laser light L by using a second main surface 1 b as a laser light entrance surface, and thereby a plurality of rows of modified regions 7 is formed in the single crystal silicon substrate 11 along each of a plurality of lines 5 to cut, and a fracture 31 is formed in the object 1 along each of the plurality of lines 5 to cut. A plurality of rows of modified regions 7 formed along each of the plurality of lines 5 to cut is arranged in the thickness direction of the object 1. Each of the plurality of rows of modified regions 7 is constituted by a plurality of modified spots 7 a arranged along the line 5 to cut (see FIG. 21). The fracture 31 extends between one row of modified regions 7 on the second main surface 1 b side and the second main surface 1 b, and between the modified regions 7 adjacent to each other among the plurality of rows of modified regions 7. Further, the fracture 31 extends between the modified spots 7 a adjacent to each other among the plurality of modified spots 7 a (see FIG. 21).

After the second step, as a third step, as illustrated in FIG. 39(b), an etching protection layer 23 in which the fracture 31 is formed along each of the plurality of lines 5 to cut is formed on the second main surface 1 b of the object 1. If an etching protection layer 23 made of SiO₂ is formed on the second main surface 1 b of the object 1 by vapor deposition, for example, a fracture 31 is formed in the etching protection layer 23 to continue to the fracture 31 formed in the object 1, and the fracture 31 reaches a surface 23 a (outer surface on an opposite side of the single crystal silicon substrate 11) of the etching protection layer 23. Here, the fracture 31 formed in the etching protection layer 23 along each of the plurality of lines 5 to cut functions as a gas passage region in the etching protection layer 23.

The subsequent steps are similar to the steps subsequent to the third step of the object cutting method according to the above-described first embodiment. Thus, the subsequent steps will be explained with reference to FIGS. 23 to 25. After the third step, as a fourth step, as illustrated in FIG. 23(a), dry etching is performed on the object 1 from the second main surface 1 b side in a state where the etching protection layer 23 is formed on the second main surface 1 b, and thereby a groove 32 is formed in the object 1 along each of the plurality of lines 5 to cut, as illustrated in FIG. 23(b). The groove 32 is, for example, a V groove (groove having a V-shaped section) opening to the second main surface 1 b. Here, dry etching is performed on the object 1 from the second main surface 1 b side with XeF₂ (that is, reactive gas etching with XeF₂ is performed). Here, dry etching is performed on the object 1 from the second main surface 1 b side such that the etching protection layer 23 remains. Further, here, the dry etching is performed on the object 1 from the second main surface 1 b such that one row of modified regions 7 on the second main surface 1 b side among the plurality of rows of modified regions 7 is removed, and thereby an uneven region 9 having an uneven shape corresponding to the one removed row of modified regions 7 is formed in the inner surface of the groove 32. In a case of forming the uneven region 9, dry etching is preferably performed until the modified region 7 (modified spot 7 a) is completely removed from the inner surface of the groove 32. Preferably, dry etching is not performed until the uneven region 9 is completely removed.

After the fourth step, as a fifth step, as illustrated in FIG. 24(a), an extension film 22 is stuck to a surface 23 a of the etching protection layer 23 (that is, stuck to the second main surface 1 b side of the object 1), and, as illustrated in FIG. 24(b), the protective film 21 is removed from the first main surface 1 a of the object 1. As illustrated in FIG. 25(a), if the extension film 22 is extended, the object 1 is cut into a plurality of semiconductor chips 15 along each of the plurality of lines 5 to cut. Then, as illustrated in FIG. 25(b), the semiconductor chips 15 are picked up.

The configuration of the semiconductor chip 15 obtained by the object cutting method according to the above-described second embodiment is similar to the configuration (see FIGS. 26 and 27) of the semiconductor chip 15 obtained by the object cutting method according to the above-described first embodiment.

As described above, according to the second embodiment, the object cutting method includes the first step of preparing the object 1 including the single crystal silicon substrate 11 and the functional device layer 12 provided on the first main surface 1 a side, the second step of irradiating the object 1 with laser light L to form at least one row of modified regions 7 in the single crystal silicon substrate 11 along each of the plurality of lines 5 to cut and to form the fracture 31 in the object 1 so as to extend between the at least one row of modified regions 7 and the second main surface 1 b of the object 1 along each of the plurality of lines 5 to cut, and the fourth step of, after the second step, performing dry etching on the object 1 from the second main surface 1 b side to form the groove 32 opening to the second main surface 1 b, in the object 1 along each of the plurality of lines 5 to cut.

In the object cutting method, the dry etching is performed from the second main surface 1 b side, on the object 1 in which the fracture 31 is formed to extend between the at least one row of modified regions 7 and the second main surface 1 b of the object 1. Thus, the dry etching selectively progresses from the second main surface 1 b along the fracture 31, and the groove 32 in which an opening is narrow in width and deep is formed along each of the plurality of lines 5 to cut. Thus, it is possible to reliably cut the object 1 into the plurality of semiconductor chips 15 along each of the lines 5 to cut, by extending the extension film 22 stuck to the second main surface 1 b side to which the groove 32 opens, for example.

In the fourth step, dry etching is performed from the second main surface 1 b such that the at least one row of modified regions 7 is removed, and the uneven region which has an uneven shape corresponding to the removed modified region 7 and in which single crystal silicon is exposed is formed in the inner surface of the groove 32. Thus, since the uneven region 9 in which single crystal silicon is exposed is formed, it is possible to suppress a decrease of strength in the vicinity of the uneven region 9.

After the second step, as the third step, the etching protection layer 23 in which the gas passage region (Here, fracture 31) is formed along each of the plurality of lines 5 to cut is formed on the second main surface 1 b. In the fourth step, dry etching is performed with XeF₂ from the second main surface 1 b, in a state where the etching protection layer 23 in which the gas passage region is formed along each of the plurality of lines to cut is formed is formed on the second main surface 1 b. Accordingly, it is possible to cause dry etching to selectively progress with higher efficiency and to form the groove 32 having an opening which is narrow in width and is deep, with higher efficiency.

In particular, in a case where the fracture 31 is formed in the etching protection layer 23 to follow the fracture 31 formed in the object 1, it is possible to save labor, for example, for forming a slit in the etching protection layer 23 by performing patterning on the etching protection layer 23.

In the fourth step, dry etching is performed from the second main surface 1 b side such that the etching protection layer 23 remains. Thus, it is possible to cause the etching protection layer 23 to function as a strong reinforcing layer or a gettering layer for capturing impurities, in the semiconductor chip 15. In a case where the etching protection layer 23 is made of metal, it is possible to cause the etching protection layer 23 to function as an electrode layer in the semiconductor chip 15. Further, it is possible to maintain the original thickness of the single crystal silicon substrate 11, in the semiconductor chip 15. In the fourth step, dry etching may be performed from the second main surface 1 b side to remove the etching protection layer 23. According to this configuration, it is possible to prevent an occurrence of an unnecessary influence by the etching protection layer 23, in the semiconductor chip 15.

In the second step, since the plurality of rows of modified regions 7 arranged in the thickness direction of the object 1 is formed, at least one row of modified regions 7 is formed along each of the plurality of lines 5 to cut, and the fracture 31 is formed to extend between the modified regions 7 adjacent to each other among the plurality of rows of modified regions 7. Thus, it is possible to cause dry etching to selectively progress deeper. In this case, in the third step, dry etching is performed from the second main surface 1 b side such that modified regions 7 on the second main surface 1 b side among the plurality of rows of modified regions 7 are removed, and thereby the uneven region 9 having an uneven shape corresponding to the removed modified region 7 is formed in the inner surface of the groove 32.

In the second step, the at least one row of modified regions 7 may be formed along each of the plurality of lines 5 to cut by forming the plurality of modified spots 7 a arranged along each of the plurality of lines 5 to cut, and the fracture 31 may be formed to extend between modified spots 7 a adjacent to each other among the plurality of rows of modified spots 7 a. Thus, it is possible to cause the dry etching to selectively progress with higher efficiency.

In a fifth step, the object 1 is cut into the plurality of semiconductor chips 15 along each of the plurality of lines 5 to cut by sticking the extension film 22 to the second main surface 1 b side and extending the extension film 22. Thus, it is possible to reliably cut the object 1 into the plurality of semiconductor chips 15 along each of the lines 5 to cut. Further, since the plurality of semiconductor chips 15 is spaced from each other on the extension film 22, it is possible to easily pick the semiconductor chips 15 up.

The semiconductor chip 15 includes the single crystal silicon substrate 110 and the functional device layer 120 provided on the first surface 110 a side of the single crystal silicon substrate 110. The second portion 112 on at least the second surface 110 b side in the single crystal silicon substrate 110 has a shape which becomes thinner as becoming farther from the first surface 110 a. The uneven region 9 which has an uneven shape and in which single crystal silicon is exposed is formed in the side surface 112 a of the second portion 112 to have a band shape.

In the semiconductor chip 15, it is possible to cause the uneven region 9 to function as a gettering region of capturing impurities. Since single crystal silicon is exposed in the uneven region 9, it is possible to suppress the decrease of strength in the vicinity of the uneven region 9.

For example, a pressure-sensitive tape having vacuum resistance, a UV tape, or the like can be used as the protective film 21. Instead of the protective film 21, a wafer fixing jig having etching resistance may be used.

It is not necessary that the material of the etching protection layer 23 is a material having transparency to laser light L. As the etching protection layer 23, the embodiment is not limited to forming of a SiO₂ film on the second main surface 1 b of the object 1, for example. For example, a resist film or a resin film may be formed on the second main surface 1 b of the object 1 by spin coating, or a metal film (Au film, Al film, or the like) may be formed on the second main surface 1 b of the object 1 by sputtering. If the etching protection layer 23 is formed on the second main surface 1 b of the object 1 by the above methods, a fracture 31 is formed in the etching protection layer 23 to continue to the fracture 31 formed in the single crystal silicon substrate 11, and the fracture 31 reaches the surface 23 a of the etching protection layer 23. That is, the fracture 31 is formed in the etching protection layer 23 without burying the fracture 31 formed in the single crystal silicon substrate 11 with the material of the etching protection layer 23. At this time, even though the material of the etching protection layer 23 enters into the fracture 31 formed in the single crystal silicon substrate 11, a practical problem in the subsequent steps does not occur so long as the fracture 31 formed in the single crystal silicon substrate 11 is not buried with the material of the etching protection layer 23.

The gas passage region formed in the etching protection layer 23 along each of the plurality of lines 5 to cut is not limited to the fracture 31. As the gas passage region, for example, a slit for exposing the second main surface 1 b of the object 1 may be formed by performing patterning on the etching protection layer 23, or a modified region (region including multiple microcracks, ablation region, and the like) may be formed by performing irradiation with laser light L.

The number of rows of modified regions 7 formed in the single crystal silicon substrate 11 along each of the plurality of lines 5 to cut is not limited to a plurality of rows and may be one row. That is, at least one row of modified regions 7 may be formed in the single crystal silicon substrate 11 along each of the plurality of lines 5 to cut. In a case where a plurality of rows of modified regions 7 is formed in the single crystal silicon substrate 11 along each of the plurality of lines 5 to cut, the modified regions 7 adjacent to each other may be connected to each other.

The fracture 31 may be formed to extend between at least one row of modified regions 7 and the second main surface 1 b of the object 1. That is, the fracture 31 may not reach the second main surface 1 b if the fracture is partial. Further, if the fracture 31 is partial, the fracture 31 may not extend between the modified regions 7 adjacent to each other and may not extend between the modified spots 7 a adjacent to each other. The fracture 31 may or may not reach the first main surface 1 a of the object 1.

Dry etching may be performed from the second main surface 1 b side to remove the etching protection layer 23. Dry etching may be performed from the second main surface 1 b side such that the plurality of rows of modified regions 7 is removed, and thereby the uneven region 9 which has an uneven shape corresponding to the plurality of rows of removed modified regions 7 and in which single crystal silicon is exposed is formed in the inner surface of the groove 32. The type of dry etching is not limited to reactive gas etching with XeF₂. As dry etching, for example, reactive ion etching with CF₄ or reactive ion etching with SF₆ may be performed.

In a case where the plurality of rows of modified regions 7 is formed in the single crystal silicon substrate 11 along each of the plurality of lines 5 to cut, dry etching may be performed, as illustrated in FIG. 28(a), such that the etching protection layer 23 remains, and some modified regions 7 are removed. Alternatively, dry etching may be performed such that the etching protection layer 23 remains, and all the modified regions 7 are removed, as illustrated in FIG. 28(b).

Alternatively, dry etching may be performed such that the etching protection layer 23 remains, and the object 1 is completely divided, as illustrated in FIG. 28(c).

In a case where the plurality of rows of modified regions 7 is formed in the single crystal silicon substrate 11 along each of the plurality of lines 5 to cut, dry etching may be performed, as illustrated in FIG. 29(a), such that the etching protection layer 23 remains, and the sectional shape of the groove 32 has a U-shape. Alternatively, dry etching may be performed such that the etching protection layer 23 remains, and the sectional shape of the groove 32 has an I-shape, as illustrated in FIG. 29(b).

In a case where the plurality of rows of modified regions 7 is formed in the single crystal silicon substrate 11 along each of the plurality of lines 5 to cut, thy etching may be performed, as illustrated in FIG. 30(a), such that the etching protection layer 23 is removed, and some modified regions 7 are removed. Alternatively, dry etching may be performed such that the etching protection layer 23 is removed, and all the modified regions 7 are removed, as illustrated in FIG. 30(b). Alternatively, dry etching may be performed such that the etching protection layer 23 is removed, and the object 1 is completely divided, as illustrated in FIG. 30(c).

In a case where the plurality of rows of modified regions 7 is formed in the single crystal silicon substrate 11 along each of the plurality of lines 5 to cut, dry etching may be performed, as illustrated in FIG. 31(a), such that the etching protection layer 23 is removed, and the sectional shape of the groove 32 has a U-shape. Alternatively, dry etching may be performed such that the etching protection layer 23 is removed, and the sectional shape of the groove 32 has an I-shape, as illustrated in FIG. 31(b).

In a case where dry etching is performed such that the object 1 is completely divided (see FIGS. 28(c), 29(b), 30(c), and 31(b)), it is not necessary that the extension film 22 is extended. However, in order to easily pick the semiconductor chip 15 up, the extension film 22 may be extended, and thus the plurality of semiconductor chips 15 on the extension film 22 may be spaced from each other.

In the semiconductor chip 15, as illustrated in FIG. 32, at least one row of uneven regions 9 may be formed to have a band shape in the side surface 110 c of the single crystal silicon substrate 110, without the modified region 7 remaining. The uneven region 9 is formed by removing all of the modified regions 7 formed in the single crystal silicon substrate 11 of the object 1 by dry etching (see FIGS. 30(b) and 30(c)). Such a semiconductor chip 15 is obtained, for example, in a case where dry etching is performed from the second main surface 1 b to completely divide the object 1. In the semiconductor chip 15 illustrated in FIG. 32, the entirety of the single crystal silicon substrate. 110 has a shape which becomes thinner as becoming farther from the first surface 110 a. That is, the entirety of the side surface 110 c of the single crystal silicon substrate 110 corresponds to the inner surface of the groove 32 formed in the single crystal silicon substrate 11 of the object 1 (see FIGS. 30(b) and 30(c)). As an example, the entirety of the single crystal silicon substrate 110 has a quadrangular pyramid shape which becomes thinner as becoming farther from the first surface 110 a. The semiconductor chip 15 illustrated in FIG. 32 may include the etching protection layer 230 formed on the second surface 110 b of the single crystal silicon substrate 110.

A second step as follows may be performed instead of the above-described second step. That is, as a second step, as illustrated in FIG. 40(a), the object 1 is irradiated with laser light L by using a first main surface 1 a as a laser light entrance surface, and thereby at least one row of modified regions 7 is formed in the single crystal silicon substrate 11 along each of a plurality of lines 5 to cut, and a fracture 31 is formed in the object 1 along each of the plurality of lines 5 to cut, so as to extend between the at least one row of modified regions 7 and the second main surface 1 b of the object 1. As illustrated in FIG. 40(b), another protective film 21 is stuck to the first main surface 1 a, and the protective film 21 which has been previously stuck is removed from the second main surface 1 b. The subsequent steps are similar to the steps subsequent to the third step described above.

In a case where the material of the protective film 21 stuck to the first main surface 1 a of the object 1 is a material having transparency to laser light L, the object 1 may be irradiated with the laser light L through the protective film 21, as illustrated in FIG. 41.

An object cutting method as follows can be performed. With the object cutting method as follows, it is also possible to reliably cut the object 1 into a plurality of semiconductor chips 15.

Firstly, as a first step, as illustrated in FIG. 42(a), an object to be processed 1 including a single crystal silicon substrate 11 and a functional device layer 12 provided on a first main surface 1 a side is prepared, and a protective film 21 is stuck to a second main surface 1 b of the object 1.

After the first step, as a second step, the object 1 is irradiated with laser light L by using a first main surface 1 a as a laser light entrance surface, and thereby at least one row of modified regions 7 is formed in the single crystal silicon substrate 11 along each of a plurality of lines 5 to cut, and a fracture 31 is formed in the object 1 along each of the plurality of lines 5 to cut, so as to extend between the at least one row of modified regions 7 and the first main surface 1 a.

After the second step, as a third step, as illustrated in FIG. 42(b), an etching protection layer 23 in which the fracture 31 is formed along each of the plurality of lines 5 to cut is formed on the first main surface 1 a of the object 1. If the etching protection layer 23 made of SiO₂ is formed on the first main surface 1 a of the object 1 by vapor deposition, for example, a fracture 31 is for in the etching protection layer 23 to continue to the fracture 31 formed in the object 1, and the fracture 31 reaches a surface 23 a (outer surface on an opposite side of the single crystal silicon substrate 11) of the etching protection layer 23. Here, the fracture 31 formed in the etching protection layer 23 along each of the plurality of lines 5 to cut functions as a gas passage region in the etching protection layer 23.

The subsequent steps are similar to the steps subsequent to the third step in the object cutting method according to the above-described modification example of the first embodiment. Thus, the subsequent steps will be explained with reference to FIGS. 37 and 38. After the third step, as the fourth step, as illustrated in FIG. 37(a), dry etching is performed on the object 1 from the first main surface 1 a side in a state where the etching protection layer 23 is formed on the first main surface 1 a, and thereby a groove 32 is formed in the object 1 along each of the plurality of lines 5 to cut, as illustrated in FIG. 37(b). The groove 32 is, for example, a V groove (groove having a V-shaped section) opening to the first main surface 1 a. Here, dry etching is performed on the object 1 from the first main surface 1 a side such that the etching protection layer 23 remains. However, dry etching may be performed on the object 1 from the first main surface 1 a side to remove the etching protection layer 23.

Performing dry etching on the object 1 from the first main surface 1 a side has the meaning that dry etching is performed on the single crystal silicon substrate 11 in a state where the second main surface 1 b is covered with the protective film and the like, and the first main surface 1 a (or etching protection layer 23 in which a gas passage region is formed along each of the plurality of lines 5 to cut) is exposed to an etching gas. In particular, in a case of performing reactive ion etching (plasma etching), performing dry etching means irradiation of the first main surface 1 a (or etching protection layer 23 in which the gas passage region is formed along each of the plurality of lines 5 to cut) with reactive species in plasma.

After the fourth step, as the fifth step, as illustrated in FIG. 38(a), the object 1 is cut into a plurality of semiconductor chips 15 along each of the plurality of lines 5 to cut by extending the protective film 21 stuck to the second main surface 1 b of the object 1, as the extension film 22. Then, as illustrated in FIG. 38(b), the semiconductor chips 15 are picked up.

Third Embodiment

An object cutting method according to a third embodiment will be explained. Constituents illustrated in FIGS. 43 to 51 are schematic, and an aspect ratio and the like of each constituent are different from those of the practical one. Firstly, as a first step, as illustrated in FIG. 43(a), an object to be processed 1 including a single crystal silicon substrate 11 and a functional device layer 12 provided on a first main surface 1 a side is prepared, and a protective film 21 is stuck to a first main surface 1 a of the object 1.

After the first step, as a second step, as illustrated in FIG. 43(b), the object 1 is irradiated with laser light L by using a second main surface 1 b as a laser light entrance surface, and thereby a plurality of rows of modified regions 7 is formed in the single crystal silicon substrate 11 along each of a plurality of lines 5 to cut, and a fracture 31 is formed in the object 1 along each of the plurality of lines 5 to cut. A plurality of rows of modified regions 7 formed along each of the plurality of lines 5 to cut is arranged in the thickness direction of the object 1. Each of the plurality of rows of modified regions 7 is constituted by a plurality of modified spots 7 a arranged along the line 5 to cut (see FIG. 21). The fracture 31 extends between one row of modified regions 7 on the second main surface 1 b side and the second main surface 1 b, and extends between the modified spots 7 a adjacent to each other among a plurality of modified spots 7 a constituting the at least one row of modified regions 7 (see FIG. 21).

The fracture 31 reaching the second main surface 1 b is cut off between the modified regions 7 adjacent to each other, as explained next. That is, in the second step, the plurality of rows of modified regions 7 is formed such that a not-fracture region M in which fractures 31 are not connected is formed at a predetermined position in the thickness direction in the object 1. The not-fracture region M is a region which has a single crystal structure and in which the modified region 7 is not formed, and is a region in which a connection between the fractures 31 is broken. The not-fracture region M is a region in which the continuous progress of the fracture 31 in the thickness direction is stopped. The predetermined position is a position of a preset and desired (any) depth.

In the example illustrated in FIGS. 43 to 51, the plurality of rows of modified regions 7 includes a modified region (first modified region) 7 closer to the first main surface 1 a side than the predetermined position being a central position in the thickness direction of the object 1, and a modified region (second modified region) 7 closer to the second main surface 1 b side than the predetermined position. In the second step, in the single crystal silicon substrate 11, the plurality of rows of modified regions 7 is formed such that a not-fracture region M in which a fracture 31 extending from the modified region 7 on the first main surface 1 a side is not connected to a fracture 31 extending from the modified region 7 on the second main surface 1 b side is formed at the predetermined position. Formation order of the plurality of rows of modified regions 7 is not particularly limited. The plurality of rows of modified regions 7 may be formed in order from the first main surface 1 a side or may be formed in order from the second main surface 1 b side.

At least some of the plurality of rows of modified regions 7 may be simultaneously formed.

An example of processing conditions in the second step will be explained. When each of the modified regions 7 was formed, laser light L having a wavelength of 1064 nm or longer (here, 1342 nm) oscillated in a pulsating manner. The pulse width of the laser light L was set to 90 ns, and the frequency thereof was set to 90 kHz. A converging point P of the laser light L was moved at a processing speed of 340 mm/s along the line 5 to cut, to be relative to the object 1. A distance (processing pitch) between modified spots formed by irradiation with one pulse of laser light L was set to 3.78 Energy of the laser light L was set to be 4 μJ to 15 μJ. The width of the modified region 7 in the thickness direction was set to be 20 μm to 56 μm. Each of the modified regions 7 was formed such that the width of the not-fracture region M in the thickness direction was set to be 10% to 30% of the thickness of the single crystal silicon substrate 11. A (100) plane was set as the first main surface 1 a.

After the second step, as the third step, as illustrated in FIG. 44(a), dry etching is performed on the object 1 from the second main surface 1 b side, and thereby a groove 32 is formed in the object 1 along each of the plurality of lines 5 to cut, as illustrated in FIG. 44(b). The groove 32 is, for example, a V groove (groove having a V-shaped section) opening to the second main surface 1 b. Here, dry etching is performed on the object 1 from the second main surface 1 b side with XeF₂ (that is, reactive gas etching with XeF₂ is performed). Here, the dry etching is performed on the object 1 from the second main surface 1 b such that one row of modified regions 7 on the second main surface 1 b side among the plurality of rows of modified regions 7 is removed, and thereby an uneven region 9 having an uneven shape corresponding to the one removed row of modified regions 7 is formed in the inner surface of the groove 32. In a case of forming the uneven region 9, dry etching is preferably performed until the modified region 7 (modified spot 7 a) is completely removed from the inner surface of the groove 32. Preferably, dry etching is not performed until the uneven region 9 is completely removed. If the fracture 31 reaches the second main surface 1 b, in a range in which the fractures 31 are connected to each other, dry etching selectively progresses from the second main surface 1 b along the fracture 31, but the selective progress of dry etching is stopped in the not-fracture region M in which the fracture 31 is cut off. Stopping the selective progress of dry etching means that a progress speed of dry etching decreases.

In the third step, dry etching is ended in a period from a time when the groove 32 reaches the second main surface 1 b side of the not-fracture region M until the groove 32 reaches the first main surface 1 a side of the not-fracture region M. In other words, in the third step, the dry etching is ended in a period from a start of dry etching on the not-fracture region M until dry etching is completed (until the entirety of the not-fracture region M is removed). In the third step, dry etching is ended before the bottom of the formed groove 32 reaches the fracture 31 extending from the modified region 7 on the first main surface 1 a side after reaching the not-fracture region M. In the third step, the groove 32 which has a curved portion at the position of the not-fracture region M and has a section of a V-shape is formed.

After the third step, as the fourth step, as illustrated in FIG. 45(a), an extension film 22 is stuck to the second main surface 1 b side of the object 1, and, as illustrated in FIG. 45(b), the protective film 21 is removed from the first main surface 1 a of the object 1. As illustrated in FIG. 46(a), the object 1 is cut into a plurality of semiconductor chips 15 along each of the plurality of lines 5 to cut, by extending the extension film 22. Then, as illustrated in FIG. 46(b), the semiconductor chips 15 are picked up.

The configuration of the semiconductor chip 15 obtained by the object cutting method according to the above-described third embodiment is similar to the configuration (see FIGS. 26 and 27) of the semiconductor chip 15 obtained by the object cutting method according to the above-described first embodiment.

As described above, in the object cutting method according to the third embodiment, dry etching is performed from the second main surface 1 b side, on the object 1 in which the fracture 31 is formed to extend between the at least one row of modified regions 7 and the second main surface 1 b. Thus, the dry etching selectively progresses from the second main surface 1 b along the fracture 31, and the groove 32 in which an opening is narrow in width and deep is formed along each of the plurality of lines 5 to cut. Here, it is known that the progress of dry etching in the not-fracture region M in which the fractures 31 are not connected in the object 1 is delayed in comparison to the progress of dry etching along the fracture 31. Thus, if the modified regions 7 are formed such that the not-fracture region M is formed at the predetermined position, it is possible to cause the not-fracture region M as an etching stopper in dry etching after that, and to reliably delay the progress of dry etching at the predetermined position.

Accordingly, according to the object cutting method according to the third embodiment, it is possible to control the progress of dry etching. It is possible to reliably stop the selective progress of dry etching at any position and to perform etching dicing with high quality. It is possible to prevent wraparound of an etching gas into the functional device layer 12. It is possible to suppress an occurrence of variations in depth of each groove 32 along each of the plurality of lines 5 to cut in comparison to a case where the not-fracture region M is not formed.

In the object cutting method according to the third embodiment, the modified region 7 closer to the first main surface 1 a side than the predetermined position and the modified region 7 closer to the second main surface 1 b side are formed. In the second step, in the single crystal silicon substrate 11, the modified regions 7 are formed such that the not-fracture region M in which the fracture 31 extending from the modified region 7 on the first main surface 1 a side is not connected to the fracture 31 extending from the modified region 7 on the second main surface 1 b side is formed at the predetermined position. According to this configuration, specific formation of the not-fracture region M is realized.

In the second step, the at least one row of modified regions 7 may be formed along each of the plurality of lines 5 to cut by forming the plurality of modified spots 7 a arranged along each of the plurality of lines 5 to cut, and the fracture 31 may be formed to extend between modified spots 7 a adjacent to each other among the plurality of rows of modified spots 7 a. According to this configuration, it is possible to cause the dry etching to selectively progress with higher efficiency.

In the second step, dry etching is ended in a period from a time when the groove 32 reaches the second main surface 1 b side of the not-fracture region M until the groove 32 reaches the first main surface 1 a side of the not-fracture region M. Thus, it is possible to end the progress of dry etching at the predetermined position (to turn into a state where etching progresses no more).

In the second step, the groove 32 which has a curved portion at the position of the not-fracture region M and has a section of a V-shape is formed by performing dry etching. Thus, it is possible to form the groove 32 which has a shape depending on the position of the not-fracture region M and has a section of a V-shape. Division by extending the extension film 22 is easily performed by the section of a V-shape, and it is possible to improve a division ratio.

In the fourth step, the object 1 is cut into the plurality of semiconductor chips 15 along each of the plurality of lines 5 to cut by sticking the extension film 22 to the second main surface 1 b side and extending the extension film 22. Thus, it is possible to reliably cut the object 1 into the plurality of semiconductor chips 15 along each of the lines 5 to cut. Further, since the plurality of semiconductor chips 15 is spaced from each other on the extension film 22, it is possible to easily pick the semiconductor chips 15 up.

In the second step, in a case where the object 1 is cut along the line 5 to cut without performing dry etching on the not-fracture region M, the modified region 7 may be formed such that, among a pair of cut surfaces of the object 1 which has been cut, a protrusion portion is formed at least a portion of the not-fracture region M on one cut surface, and a recessed portion corresponding to the protrusion portion is formed at least a portion of the not-fracture region M on the other cut surface. Examples of the case where the object 1 is cut along the line 5 to cut without performing dry etching on the not-fracture region M include a case where the fourth step is temporarily performed after the second step without performing the third step in order to check quality. According to this configuration, it is possible to reliably cause the fractures not to be connected to each other in the not-fracture region M. The height of the protrusion portion may be 2 μm to 6 μm. The width of the protrusion portion in the thickness direction may be 6 μm to 17 μm. The cut surface 12 c may be a (110) plane, and the surface on which the protrusion portion is formed may be a (111) plane. Such a recessed portion or a protrusion portion is referred to as a black streak because the recessed portion or the protrusion portion can be observed like the black streak if observing by an optical microscope.

In a case where a laser processing apparatus that performs the object cutting method according to the third embodiment includes a spatial light modulator such as a reflective spatial light modulator, in the second step, the modified region 7 may be formed to form the not-fracture region M at the predetermined position, by appropriately setting a modulation pattern of the spatial light modulator instead or in addition to the above process.

For example, the modified regions 7 may be formed between a position on the first main surface 1 a side and a position on the second main surface 1 b side such that the not-fracture region M is formed at the predetermined position by irradiation with laser light L which is modulated with the following modulation pattern by the spatial light modulator after the modified region 7 on the first main surface 1 a side is formed and before the modified region 7 on the second main surface 1 b side is formed. The modulation pattern may include at least one of a quality pattern, an individual difference correction pattern, a spherical aberration correction pattern, and an astigmatism correction pattern, as an element pattern. The modulation pattern may include a quality pattern which has a first brightness region extending in a direction intersecting with the line 5 to cut and a second brightness region adjacent to both sides of the first brightness region in an extension direction of the line 5 to cut.

In the second step, in the single crystal silicon substrate 11, the modified regions 7 may be formed such that a not-fracture region M in which a fracture 31 extending from the modified region 7 on the first main surface 1 a side is not connected to the modified region 7 on the second main surface 1 b side or a not-fracture region M in which a fracture 31 extending from the modified region 7 on the second main surface 1 b is not connected to the modified region 7 on the first main surface 1 a side are formed at predetermined positions.

For example, a pressure-sensitive tape having vacuum resistance, a UV tape, or the like can be used as the protective film 21. Instead of the protective film 21, a wafer fixing jig having etching resistance may be used.

Before dry etching is performed, the etching protection layer in which the gas passage region is formed along each of the plurality of lines 5 to cut may be formed on the second main surface 1 b of the object 1. In a case where the object 1 is irradiated with laser light L through the etching protection layer, it is necessary that the material of the etching protection layer is a material having transparency to the laser light L. As the etching protection layer, for example, a SiO₂ film may be formed on the second main surface 1 b of the object 1 by vapor deposition, a resist film or a resin film may be formed on the second main surface 1 b of the object 1 by spin coating, or a sheet-like member (transparent resin film and the like) and a rear-surface protection tape (IRLC tape/WP tape) may stick to the second main surface 1 b of the object 1. As the gas passage region, for example, the fracture 31 may be caused to reach the surface (outer surface on an opposite side of the single crystal silicon substrate) of the etching protection layer from the modified region 7 while the modified region 7 is formed in the single crystal silicon substrate 11, by irradiating the object 1 with laser light L through the etching protection layer. Alternatively, a slit for exposing the second main surface 1 b of the object 1 may be formed by performing patterning on the etching protection layer, or the modified region (region including multiple microcracks, ablation region, and the like) may be formed by performing irradiation with laser light L.

The fracture 31 may be formed to extend between at least one row of modified regions 7 and the second main surface 1 b of the object 1. That is, the fracture 31 may not reach the second main surface 1 b if the fracture is partial. Further, the fracture 31 may not extend between the modified spots 7 a adjacent to each other so long as the fracture 31 is partial. The fracture 31 may or may not reach the first main surface 1 a of the object 1.

Dry etching may be performed from the second main surface 1 b side such that the plurality of rows of modified regions 7 is removed, and thereby the uneven region 9 which has an uneven shape corresponding to the plurality of rows of removed modified regions 7 and in which single crystal silicon is exposed is formed in the inner surface of the groove 32. The type of dry etching is not limited to reactive gas etching with XeF₂. As dry etching, for example, reactive ion etching with CF₄ or reactive ion etching with SF₆ may be performed.

As illustrated in FIGS. 47(a) and 47(b), dry etching may be performed such that the sectional shape of the groove 32 is a V-shape. Alternatively, as illustrated in FIGS. 48(a) and 48(b), dry etching may be performed such that the sectional shape of the groove 32 is a U-shape. Alternatively, as illustrated in FIGS. 49(a) and 49(b), dry etching may be performed such that the sectional shape of the groove 32 is an I-shape.

A first step and a second step as follows may be performed instead of the first step and the second step described above. That is, as the first step, as illustrated in FIG. 50(a), an object to be processed 1 is prepared, and a protective film 21 is stuck to a second main surface 1 b of the object 1. After the first step, as a second step, the object 1 is irradiated with laser light L by using a first main surface 1 a as a laser light entrance surface, and thereby a plurality of rows of modified regions 7 is formed in the single crystal silicon substrate 11 along each of a plurality of lines 5 to cut, and a fracture 31 is formed in the object 1 along each of the plurality of lines 5 to cut. As illustrated in FIG. 50(b), another protective film 21 is stuck to the first main surface 1 a, and the protective film 21 which has been previously stuck is removed from the second main surface 1 b. The subsequent steps are similar to the steps subsequent to the third step described above.

In a case where the material of the protective film 21 stuck to the first main surface 1 a of the object 1 is a material having transparency to laser light L, the object 1 may be irradiated with the laser light L through the protective film 21, as illustrated in FIG. 51.

Fourth Embodiment

An object cutting method according to a fourth embodiment will be explained. Constituents illustrated in FIGS. 52 to 55 are schematic, and an aspect ratio and the like of each constituent are different from those of the practical one. A first step and a second step are similar to the steps illustrated in FIGS. 7(a) and 7(b). That is, as the first step, as illustrated in FIG. 7(a), an object to be processed 1 including a single crystal silicon substrate 11 and a functional device layer 12 provided on a first main surface 1 a side is prepared, and a protective film 21 is stuck to a first main surface 1 a of the object 1.

After the first step, as the second step, as illustrated in FIG. 7(b), the object 1 is irradiated with laser light L by using a second main surface 1 b as a laser light entrance surface, and thereby a plurality of rows of modified regions 7 is formed in the single crystal silicon substrate 11 along each of a plurality of lines 5 to cut, and a fracture 31 is formed in the object 1 along each of the plurality of lines 5 to cut. A plurality of rows of modified regions 7 formed along each of the plurality of lines 5 to cut is arranged in the thickness direction of the object 1. Each of the plurality of rows of modified regions 7 is constituted by a plurality of modified spots 7 a arranged along the line 5 to cut (see FIG. 21). The fracture 31 extends between one row of modified regions 7 on the second main surface 1 b side and the second main surface 1 b, and between the modified regions 7 adjacent to each other among the plurality of rows of modified regions 7. Further, the fracture 31 extends between the modified spots 7 a adjacent to each other among the plurality of modified spots 7 a (see FIG. 21).

After the second step, as a third step, as illustrated in FIG. 52(a), reactive ion etching is performed on the object 1 from the second main surface 1 b side, and thereby a groove 32 is formed in the object 1 along each of the plurality of lines 5 to cut, as illustrated in FIG. 52(b). The groove 32 is, for example, a V groove (groove having a V-shaped section) opening to the second main surface 1 b. Here, dry etching is performed on the object 1 from the second main surface 1 b side with CF₄ or SF₆ (that is, reactive ion etching with CF₄ or SF₆ is performed). Here, reactive ion etching is performed on the object 1 from the second main surface 1 b such that one row of modified regions 7 on the second main surface 1 b side among the plurality of rows of modified regions 7 is removed, and thereby an uneven region 9 having an uneven shape corresponding to the one removed row of modified regions 7 is formed in the inner surface of the groove 32. In a case of forming the uneven region 9, reactive ion etching is preferably performed until the modified region 7 (modified spot 7 a) is completely removed from the inner surface of the groove 32. Preferably, reactive ion etching is not performed until the uneven region 9 is completely removed.

In the third step, as illustrated in FIG. 23(c), a black silicon layer 6 is formed on the second main surface 1 b of the object 1 and the inner surface of the groove 32 by mixing oxygen (O₂) with the etching gas (that is, CF₄ or SF₆) in the process of performing reactive ion etching. The black silicon layer 6 is provided to be stacked on the second main surface 1 b of the object 1 and is provided to enter into the groove 32. The black silicon layer 6 is provided to cover the second main surface 1 b side of the object 1. Thus, the selective progress of reactive ion etching is not stopped, and then is ended.

The black silicon layer 6 is formed by a black silicon phenomenon in which a SiO₂-based substance being a reaction product during dry etching is deposited on an etching target surface. The black silicon layer 6 includes fine needle-like unevenness. The end of reactive ion etching may mean a state where reactive ion etching progresses no more. A timing at which O₂ is mixed is a timing at which the depth of the groove 32 reaches a desired (any) predetermined depth which is set in advance. The timing at which O₂ is mixed can be set, for example, by calculation with the etching rate ratio and the like or by at least any of an experiment and an experience. The mixed amount of O₂ may be equal to or more than a predetermined amount allowing the black silicon layer 6 to be formed. The mixed amount of O₂ may be a preset constant amount or a variable amount.

After the third step, as a fourth step, as illustrated in FIG. 53(a), an extension film 22 is stuck to the black silicon layer 6 on the second main surface 1 b of the object 1 (that is, stuck to the second main surface 1 b side of the object 1), and, as illustrated in FIG. 53(b), the protective film 21 is removed from the first main surface 1 a of the object 1. As illustrated in FIG. 54(a), the object 1 is cut into a plurality of semiconductor chips 15 along each of the plurality of lines 5 to cut, by extending the extension film 22. Then, as illustrated in FIG. 54(b), the semiconductor chips 15 are picked up.

The configuration of the semiconductor chip 15 obtained by the object cutting method according to the above-described fourth embodiment is similar to the configuration (see FIGS. 26 and 27) of the semiconductor chip 15 obtained by the object cutting method according to the above-described first embodiment except that the black silicon layer 6 is formed in a region corresponding to the second main surface 1 b and the inner surface of the groove 32 in the single crystal silicon substrate 11. In the semiconductor chip 15, it is possible to cause the black silicon layer 6 to function as a gettering region of capturing impurities, in addition to the uneven region 9.

As described above, in the object cutting method according to the fourth embodiment, reactive ion etching is performed from the second main surface 1 b side, on the object 1 in which the fracture 31 is formed to extend between the at least one row of modified regions 7 and the second main surface 1 b. Thus, reactive ion etching selectively progresses from the second main surface 1 b along the fracture 31, and thus the groove 32 in which an opening is narrow in width and deep is formed along each of the plurality of lines 5 to cut. Here, the black silicon layer 6 is formed on the second main surface 1 b of the object 1 and the inner surface of the groove 32 in the process of performing reactive ion etching, and thus it is possible to end the progress of etching by using the black silicon layer 6. That is, it is possible to control the progress of dry etching. It is possible to reliably stop reactive ion etching at any timing and to perform etching dicing with high quality. Since it is possible to stop reactive ion etching in the middle of etching, it is possible to prevent wraparound of the etching gas into the functional device layer 12.

In the second step, since the plurality of rows of modified regions 7 arranged in the thickness direction of the object 1 is formed, at least one row of modified regions 7 may be formed along each of the plurality of lines 5 to cut, and the fracture 31 may be formed to extend between the modified regions 7 adjacent to each other among the plurality of rows of modified regions 7. According to this configuration, it is possible to cause reactive ion etching to selectively progress deeper.

In the second step, the at least one row of modified regions 7 may be formed along each of the plurality of lines 5 to cut by forming the plurality of modified spots 7 a arranged along each of the plurality of lines 5 to cut, and the fracture 31 may be formed to extend between modified spots 7 a adjacent to each other among the plurality of rows of modified spots 7 a. According to this configuration, it is possible to cause reactive ion etching to selectively progress with higher efficiency.

In the third step, the black silicon layer 6 is formed by mixing O₂ with the etching gas. Thus, it is possible to specifically realize formation of the black silicon layer 6.

In the third step, O₂ is mixed with the etching gas when the groove 32 has a predetermined depth. Thus, the black silicon layer 6 is formed such that the groove 32 having a predetermined depth is formed, and thus it is possible to end the progress of etching.

In the fourth step, the object 1 is cut into the plurality of semiconductor chips 15 along each of the plurality of lines 5 to cut by sticking the extension film 22 to the second main surface 1 b side and extending the extension film 22. Thus, it is possible to reliably cut the object 1 into the plurality of semiconductor chips 15 along each of the lines 5 to cut. Further, since the plurality of semiconductor chips 15 is spaced from each other on the extension film 22, it is possible to easily pick the semiconductor chips 15 up.

For example, a pressure-sensitive tape having vacuum resistance, a UV tape, or the like can be used as the protective film 21. Instead of the protective film 21, a wafer fixing jig having etching resistance may be used.

The number of rows of modified regions 7 formed in the single crystal silicon substrate 11 along each of the plurality of lines 5 to cut is not limited to a plurality of rows and may be one row. That is, at least one row of modified regions 7 may be formed in the single crystal silicon substrate 11 along each of the plurality of lines 5 to cut. In a case where a plurality of rows of modified regions 7 is formed in the single crystal silicon substrate 11 along each of the plurality of lines 5 to cut, the modified regions 7 adjacent to each other may be connected to each other.

The fracture 31 may be formed to extend between at least one row of modified regions 7 and the second main surface 1 b of the object 1. That is, the fracture 31 may not reach the second main surface 1 b if the fracture is partial. Further, if the fracture 31 is partial, the fracture 31 may not extend between the modified regions 7 adjacent to each other and may not extend between the modified spots 7 a adjacent to each other. The fracture 31 may or may not reach the first main surface 1 a of the object 1.

Dry etching may be performed from the second main surface 1 b side such that the plurality of rows of modified regions 7 is removed, and thereby the uneven region 9 which has an uneven shape corresponding to the plurality of rows of removed modified regions 7 and in which single crystal silicon is exposed is formed in the inner surface of the groove 32. As dry etching, reactive ion etching with a gas other than CF₄ or SF₆ may be performed.

An object cutting method as follows can be performed. With the object cutting method as follows, it is also possible to reliably cut the object 1 into a plurality of semiconductor chips 15.

A first step and a second step are similar to the steps illustrated in FIGS. 7(a) and 7(b). That is, as the first step, as illustrated in FIG. 7(a), an object to be processed 1 including a single crystal silicon substrate 11 and a functional device layer 12 provided on a first main surface 1 a side is prepared, and a protective film 21 is stuck to a first main surface 1 a of the object 1.

After the first step, as the second step, as illustrated in FIG. 7(b), the object 1 is irradiated with laser light L by using a second main surface 1 b as a laser light entrance surface, and thereby a plurality of rows of modified regions 7 is formed in the single crystal silicon substrate 11 along each of a plurality of lines 5 to cut, and a fracture 31 is formed in the object 1 along each of the plurality of lines 5 to cut. A plurality of rows of modified regions 7 formed along each of the plurality of lines 5 to cut is arranged in the thickness direction of the object 1. Each of the plurality of rows of modified regions 7 is constituted by a plurality of modified spots 7 a arranged along the line 5 to cut (see FIG. 21). The fracture 31 extends between one row of modified regions 7 on the second main surface 1 b side and the second main surface 1 b, and between the modified regions 7 adjacent to each other among the plurality of rows of modified regions 7. Further, the fracture 31 extends between the modified spots 7 a adjacent to each other among the plurality of modified spots 7 a (see FIG. 21).

After the second step, as a third step, as illustrated in FIG. 55(a), the black silicon layer 6 in which the fracture 31 is formed along each of the plurality of lines 5 to cut is formed on the second main surface 1 b of the object 1, as the etching protection layer. Here, the black silicon layer 6 is formed on the second main surface 1 b of the object 1 by increasing an introduction amount of oxygen (O₂) into the etching gas (CF₄, SF₆, or the like) for reactive ion etching. In this case, a fracture 31 is formed in the black silicon layer 6 to continue to the fracture 31 formed in the object 1, and the fracture 31 reaches the surface (outer surface on an opposite side of the single crystal silicon substrate 11) of the black silicon layer 6. Here, the fracture 31 formed in the black silicon layer 6 along each of the plurality of lines 5 to cut functions as a gas passage region in the black silicon layer 6.

After the third step, as the fourth step, as illustrated in FIG. 55(b), only the introduction amount of O₂ is reduced, dry etching is performed on the object 1 from the second main surface 1 b side in a state where the black silicon layer 6 is formed on the second main surface 1 b, and thereby a groove 32 is formed in the object 1 along each of the plurality of lines 5 to cut, as illustrated in FIG. 55(c). The groove 32 is, for example, a V groove (groove having a V-shaped section) opening to the second main surface 1 b. Here, dry etching is performed on the object 1 from the second main surface 1 b side by the etching gas for reactive ion etching.

The subsequent steps are similar to steps subsequent to the fifth step of the object cutting method according to the above-described fourth embodiment. Thus, the subsequent steps will be explained with reference to FIGS. 53 and 54. After the fourth step, as a fifth step, as illustrated in FIG. 53(a), an extension film 22 is stuck to the black silicon layer 6 on the second main surface 1 b of the object 1 (that is, stuck to the second main surface 1 b side of the object 1), and, as illustrated in FIG. 53(b), the protective film 21 is removed from the first main surface 1 a of the object 1. As illustrated in FIG. 54(a), the object 1 is cut into a plurality of semiconductor chips 15 along each of the plurality of lines 5 to cut, by extending the extension film 22. Then, as illustrated in FIG. 54(b), the semiconductor chips 15 are picked up.

Fifth Embodiment

An object cutting method as follows can be performed. According to a fifth embodiment, an object cutting method includes a first step of preparing an object to be processed 1 including a single crystal material substrate and a functional device layer 12 provided on a first main surface 1 a side, a second step of, after the first step, irradiating the object 1 with laser light L to form at least one row of modified regions 7 in the single crystal material substrate along each of a plurality of lines 5 to cut and to form a fracture 31 in the object 1 so as to extend between the at least one row of modified regions 7 and a second main surface 1 b of the object 1 along each of the plurality of lines 5 to cut, and a third step of, after the second step, performing dry etching on the object 1 from the second main surface 1 b side to form a groove 32 opening to the second main surface 1 b, in the object 1 along each of the plurality of lines 5 to cut. In the third step, dry etching is performed from the second main surface 1 b such that the at least one row of modified regions 7 is removed, and an uneven region which has an uneven shape corresponding to the removed modified region 7 and in which a single crystal material is exposed is formed in an inner surface of the groove 32.

In the object cutting method, the dry etching is performed from the second main surface 1 b side, on the object 1 in which the fracture 31 is formed to extend between the at least one row of modified regions 7 and the second main surface 1 b of the object 1. Thus, the dry etching selectively progresses from the second main surface 1 b along the fracture 31, and the groove 32 in which an opening is narrow in width and deep is formed along each of the plurality of lines 5 to cut. Thus, it is possible to reliably cut the object 1 into the plurality of semiconductor chips 15 along each of the lines 5 to cut, by extending the extension film 22 stuck to the second main surface 1 b side to which the groove 32 opens, for example. In addition, since the uneven region in which the single crystal material is exposed is formed by removing the at least one row of modified regions 7, it is possible to suppress a decrease of strength in the vicinity of the uneven region.

In the object cutting method according to the fifth embodiment, in the second step, the at least one row of modified regions 7 may be formed along each of the plurality of lines 5 to cut by forming a plurality of rows of modified regions 7 arranged in a thickness direction of the object 1, and the fracture 31 may be formed to extend between modified regions 7 adjacent to each other among the plurality of rows of modified regions 7. In the third step, dry etching may be performed from the second main surface 1 b such that the modified region 7 on the second main surface 1 b side among the plurality of rows of modified regions 7 is removed to form the uneven region having the uneven shape corresponding to the removed modified region 7, in the inner surface of the groove 32. According to this configuration, it is possible to cause the dry etching to selectively progress deeper.

In the object cutting method according to the fifth embodiment, in the second step, the at least one row of modified regions 7 may be formed along each of the plurality of lines 5 to cut by forming a plurality of modified spots 7 a arranged along each of the plurality of lines 5 to cut, and the fracture 31 may be formed to extend between modified spots 7 a adjacent to each other among the plurality of rows of modified spots 7 a. According to this configuration, it is possible to cause the dry etching to selectively progress with higher efficiency.

The object cutting method according to the fifth embodiment may further include, after the third step, a fourth step of cutting the object 1 into the plurality of semiconductor chips 15 along each of the plurality of lines 5 to cut by sticking an extension film 22 to the second main surface 1 b side and extending the extension film 22. According to this configuration, it is possible to reliably cut the object 1 into the plurality of semiconductor chips 15 along each of the lines 5 to cut. Further, since the plurality of semiconductor chips 15 is spaced from each other on the extension film 22, it is possible to easily pick the semiconductor chips 15 up.

REFERENCE SIGNS LIST

-   -   1 . . . object to be processed, 1 a . . . first main surface, 1         b . . . second main surface, 5 . . . line to cut, 7 . . .         modified region, 7 a . . . modified spot, 11 . . . single         crystal silicon substrate, 12 . . . functional device layer, 15         . . . semiconductor chip, 22 . . . extension film, 23 . . .         etching protection layer, 23 a . . . surface, 31 . . . fracture,         32 . . . groove, L . . . laser light 

The invention claimed is:
 1. An object cutting method comprising: a first step of preparing an object to be processed including a single crystal silicon substrate and a functional device layer provided on a first main surface side; a second step of, after the first step, irradiating the object with laser light to form at least one row of modified regions in the single crystal silicon substrate along each of a plurality of lines to cut and to form a fracture in the object so as to extend between the at least one row of modified regions and a second main surface of the object along each of the plurality of lines to cut; and a third step of, after the second step, performing dry etching on the object from the second main surface side to form a groove opening to the second main surface, in the object along each of the plurality of lines to cut, wherein, in the third step, the dry etching is performed from the second main surface side such that the at least one row of modified regions is removed to form an uneven region which has an uneven shape corresponding to the removed modified region and in which single crystal silicon is exposed, in an inner surface of the groove.
 2. The object cutting method according to claim 1, wherein, in the second step, the at least one row of modified regions is formed along each of the plurality of lines to cut by forming a plurality of rows of modified regions arranged in a thickness direction of the object, and the fracture is formed to extend between modified regions adjacent to each other among the plurality of rows of modified regions, and in the third step, the dry etching is performed from the second main surface side such that the modified region on the second main surface side among the plurality of rows of modified regions is removed to form the uneven region which has the uneven shape corresponding to the removed modified region, in the inner surface of the groove.
 3. The object cutting method according to claim 1, wherein, in the second step, the at least one row of modified regions is formed along each of the plurality of lines to cut by forming a plurality of modified spots arranged along each of the plurality of lines to cut, and the fracture is formed to extend between modified spots adjacent to each other among the plurality of modified spots.
 4. The object cutting method according to claim 1, further comprising: a fourth step of, after the third step, cutting the object into a plurality of semiconductor chips along each of the plurality of lines to cut by sticking an extension film to the second main surface side and extending the extension film.
 5. An object cutting method comprising: a first step of preparing an object to be processed including a single crystal material substrate and a functional device layer provided on a first main surface side; a second step of, after the first step, irradiating the object with laser light to form at least one row of modified regions in the single crystal material substrate along each of a plurality of lines to cut and to form a fracture in the object so as to extend between the at least one row of modified regions and a second main surface of the object along each of the plurality of lines to cut; and a third step of, after the second step, performing dry etching on the object from the second main surface side to form a groove opening to the second main surface, in the object along each of the plurality of lines to cut, wherein, in the third step, the dry etching is performed from the second main surface side such that the at least one row of modified regions is removed to form an uneven region which has an uneven shape corresponding to the removed modified region and in which a single crystal material is exposed, in an inner surface of the groove.
 6. The object cutting method according to claim 5, wherein, in the second step, the at least one row of modified regions is formed along each of the plurality of lines to cut by forming a plurality of rows of modified regions arranged in a thickness direction of the object, and the fracture is formed to extend between modified regions adjacent to each other among the plurality of rows of modified regions, and in the third step, the dry etching is performed from the second main surface side such that the modified region on the second main surface side among the plurality of rows of modified regions is removed to form the uneven region which has the uneven shape corresponding to the removed modified region, in the inner surface of the groove.
 7. The object cutting method according to claim 5, wherein, in the second step, the at least one row of modified regions is formed along each of the plurality of lines to cut by forming a plurality of modified spots arranged along each of the plurality of lines to cut, and the fracture is formed to extend between modified spots adjacent to each other among the plurality of modified spots.
 8. The object cutting method according to claim 5, further comprising: a fourth step of, after the third step, cutting the object into a plurality of semiconductor chips along each of the plurality of lines to cut by sticking an extension film to the second main surface side and extending the extension film. 